A spacer-on-spacer scheme for self-aligned multiple patterning and integration

A novel, low-cost spacer-on-spacer pitch-splitting approach is targeted at sub-32nm pitch for 7nm technology nodes and beyond.
11 August 2016
Angélique Raley, Sophie Thibaut, Nihar Mohanty, Kal Subhadeep, Satoru Nakamura, Akiteru Ko, David O'Meara, Kandabara Tapily, Steve Consiglio and Peter Biolsi

To enable lithographic printing of ever smaller features, multipatterning techniques are increasingly being used in the semiconductor industry. These techniques are designed to extend 193nm immersion lithography, which is necessary to enable designs at 20nm or below. Multipatterning methods, however, are typically two to three times more expensive for each wafer than for a theoretical 193nm-immersion-based single exposure (assuming that 193nm immersion could be used to achieve the desired pitch). Moreover, extreme UV (EUV) lithography—a technology for the 5nm node that is expected to be available after 2020—is a costly option for high-volume production at major foundries and integrated device manufacturers (see Figure 1).1

Figure 1. Normalized wafer cost adder for different multipatterning techniques, according to internal TEL calculations. Numbers in the right hand column are multiples of the cost of single exposure patterning (e.g., LELE is 2.5 times the cost of SE). SAQP: Self-aligned quadruple patterning. EUV: Extreme UV. LELELE: Litho etch litho etch litho etch.

At present, self-aligned quadruple patterning (SAQP) is the optimum technique for patterning of layers that require the most aggressive pitch shrink (such as fin formation and critical metal layers). In a standard SAQP stack, two hard mandrels are used alongside the appropriate etch stop and hardmask layers (see Figure 2). Integration of these components, however, is complex and involves several sacrificial layers that require multiple dry-etch and wet-etch steps. In response to this complexity, developers have so far made several attempts to simplify multipatterning processes, and to reduce costs and improve throughput.2, 3

Figure 2. Schematic illustration of the standard SAQP approach, in which two hard mandrels are used (associated with the appropriate etch stop and hardmask layer). This integration is complex and involves several sacrificial layers that require multiple dry- and wet-etch steps. HM: Hardmask. DARC: Dielectric antireflective coating. Litho: Lithography. PR: Photoresist.

We propose a low-cost alternative SAQP scheme that features no sacrificial layers, and which uses a spacer-on-spacer pitch-splitting strategy (see Figure 3). With our method, which requires careful selection of the underlying substrate, mandrel, and spacer materials, we can achieve a 25% reduction in cost compared with the traditional SAQP approach. In our demonstration of this technique, we took an atomic layer deposition (ALD) film material—which we used for the first spacer (spacer 1)—and successfully used it as a second mandrel. We achieved this by optimizing the spacer shape to minimize the second spacer (spacer 2) mask asymmetry, which could otherwise cause line-edge roughness (LER) degradation and could have a significant impact on the edge-placement error during the final pattern transfer. When defining the first mandrel pattern, it was necessary to select the etch process according to the underlying layer, i.e., so that it caused minimal gouging. For the same reason, we had to consider the substrate when selecting the chemistry of the spacer 1 and spacer 2 etches. After completing the spacer 2 etch, we thus removed the spacer 1 etch selectively to the spacer 2 material and to the substrate.

Figure 3. Illustration of the proposed spacer-on-spacer SAQP integration. Depo: Deposition. Pull: Removal (of spacer).

By meeting all the selectivity requirements, we demonstrated that our scheme has a superior process performance and control of pitch walking (where mask misalignment causes anomalies in the pitch) than the SAQP approach. No pattern was transferred to the underlayers (except at the last step), therefore there was minimal variation in the critical dimensions (CDs) through pattern transfer to the underlying masks. In addition, by using the ALD spacer films, we were able to further control CD variation. We used the organic litho stack material as a first mandrel, and an ALD room-temperature silicon dioxide film (which is compatible with organic materials) as a first spacer. We used a low-temperature titanium dioxide ALD film as a second spacer, and titanium as the underlying substrate for patterning.

Our scheme has a low thermal budget, and can thus easily be implemented at the ‘back end of line’ (the second stage in integrated circuit fabrication). We conducted all anisotropic etches in a capacitively coupled plasma chamber with a high-frequency power source on the top electrode and a low-frequency source on the bottom electrode. This chamber configuration enables independent control of plasma density and ion energy. We used a plasma-free gas-phase etch process tool to remove dielectric antireflective coating (DARC) and to remove spacer 1 (selective to spacer 2 and the underlayer). This tool can be used to remove both materials (DARC and silicon dioxide) with minimum damage to the underlayer and the spacer 2 mask. During this process, we introduced gases on the wafer, where they adsorbed and formed a finite layer of modified material. We then heated the wafer to sublimate the modified layer, and repeated this isotropic process in cycles until we had removed the desired amount of material. In this way, we achieved a high-selectivity, damage-free controlled etch. It is also possible to modify the gases that are used to remove various target film materials.

Our integration concept is illustrated in Figure 4 on silicon, from mandrel patterning (left) to final pattern transfer (right). In addition to cost and throughput concerns, line-width roughness (LWR) and LER are important parameters for process-performance benchmarking since they affect device performance directly.4 We compared the spacer-on-spacer SAQP pitch-splitting process performance, in terms of LER/LWR, against previously demonstrated flows,5 and found that the two were equivalent. We can execute our spacer-on-spacer integration with various permutations of the ALD spacer and mandrel materials to suit the needs of each application. In addition, it may be possible to achieve more aggressive scaling down (to 20nm pitch) without experiencing the problems of high aspect-ratio line wiggling, since all patterning is executed on the same level.

Figure 4. Scanning electron microscope images that demonstrate the spacer-on-spacer SAQP flow on silicon with 15nm lines at 30nm pitch. The images illustrate the integration process from mandrel patterning (left) to final pattern transfer (right).

In summary, we have demonstrated a spacer-on-spacer pitch-splitting SAQP integration that reduces the processing costs of standard integrations. Our method enables patterning of sub-30nm pitch applications (e.g., fins and critical layers), and—thanks to the reduced number of processing steps—it shows great potential for cost savings and throughput improvements. The key challenges that remain are the selection of appropriate materials to guarantee adequate selectivity, and engineering of the spacer shape to prevent edge-alignment errors. Our future aim is to demonstrate the feasibility of our technique at lower pitches and to explore additional material sets.

Angélique Raley, Sophie Thibaut, Nihar Mohanty, Kal Subhadeep, Satoru Nakamura, Akiteru Ko, David O'Meara, Kandabara Tapily, Steve Consiglio, Peter Biolsi
TEL Technology Center, America, LLC
Albany, NY

Angélique Raley is a senior process engineer whose research focus is on plasma etch development for advanced technology node patterning.

1. http://www.extremetech.com/computing/221532-tsmc-will-begin-10nm-production-this-year-claims-5nm-by-2020 The Taiwan Semiconductor Manufacturing Company's roadmap to achieve 5nm production. Accessed 30 June 2016.
2. Y. Chen, P. Xu, L. Miao, Y. Chen, X. Xu, D. Mao, P. Blanco, C. Bencher, R. Hung, C. S. Ngai, Self-aligned triple patterning for continuous IC scaling to half-pitch 15nm, Proc. SPIE 7973, p. 79731P, 2011. doi:10.1117/12.881645
3. N. Mohanty, E. Franke, E. Liu, A. Raley, J. Smith, R. Farrell, M. Wang, et al., Challenges and mitigation strategies for resist trim etch in resist-mandrel based SAQP integration scheme, Proc. SPIE 9428, p. 94280G, 2015. doi:10.1117/12.2085016
4. G. Leung, L. Lai, P. Gupta, C. O. Chui, Device-and circuit-level variability caused by line edge roughness for sub-32-nm FinFET technologies, IEEE Trans. Electron Devices 59, p. 2057-2063, 2012.
5. A. Raley, S. Thibaut, N. Mohanty, K. Subhadeep, S. Nakamura, A. Ko, D. O'Meara, K. Tapily, S. Consiglio, P. Biolsi, Self-aligned quadruple patterning integration using spacer on spacer pitch splitting at the resist level for sub-32nm pitch applications, Proc. SPIE 9782, p. 97820F, 2016. doi:10.1117/12.2219321
Recent News
Sign in to read the full article
Create a free SPIE account to get access to
premium articles and original research
Forgot your username?