Oxygen partial pressure influence on the character of InGaZnO thin films grown by PLD
Author(s): Yi Lu; Li Wang
Format Member Price Non-Member Price
PDF $17.00 $21.00

Paper Abstract

The amorphous oxide semiconductors (AOSs) are promising for emerging large-area optoelectronic applications because of capability of large-area, uniform deposition at low temperatures such as room temperature (RT). Indium–gallium–zinc oxide (InGaZnO) thin film is a promising amorphous semiconductors material in thin film transistors (TFT) for its excellent electrical properties. In our work, the InGaZnO thin films are fabricated on the SiO2 glass using pulsed laser deposition (PLD) in the oxygen partial pressure altered from 1 to 10 Pa at RT. The targets were prepared by mixing Ga2O3, In2O3, and ZnO powder at a mol ratio of 1: 7: 2 before the solid-state reactions in a tube furnace at the atmospheric pressure. The targets were irradiated by an Nd:YAG laser(355nm). Finally, we have three films of 270nm, 230nm, 190nm thick for 1Pa, 5Pa, 10Pa oxygen partial pressure. The product thin films were characterized by X-ray diffraction (XRD), atomic force microscopy (AFM), Hall-effect investigation. The comparative study demonstrated the character changes of the structure and electronic transport properties, which is probably occurred as a fact of the different oxygen partial pressure used in the PLD.

Paper Details

Date Published: 29 November 2012
PDF: 6 pages
Proc. SPIE 8551, High-Power Lasers and Applications VI, 855118 (29 November 2012); doi: 10.1117/12.999376
Show Author Affiliations
Yi Lu, Beijing Univ. of Technology (China)
Li Wang, Beijing Univ. of Technology (China)

Published in SPIE Proceedings Vol. 8551:
High-Power Lasers and Applications VI
Upendra N. Singh; Dianyuan Fan; Jianquan Yao; Robert F. Walter, Editor(s)

© SPIE. Terms of Use
Back to Top