Improved performance of 375 nm InGaN/AlGaN light-emitting diodes by incorporating a heavily Si-doped transition layer
Format Member Price Non-Member Price
PDF $17.00 $21.00

Paper Abstract

High performance 375-nm ultraviolet (UV) InGaN/AlGaN light-emitting diodes (LEDs) was developed using a heavy Si-doping technique with metalorganic chemical vapor deposition (MOCVD). From the transmission electron microcopy (TEM) image, the dislocation density was reduced after inserting a heavily Si-doping growth mode transition layer (GMTL) between un-doped GaN layer and Si-doped Al0.02Ga0.98N contact layer. The internal quantum efficiency (IQE) of the sample with GMTL measured by power-dependent photoluminescence shows 39.4% improved compared with the sample without GMTL. When the vertical type LED chips (size: 1mm×1mm) driving by a 350-mA current, the output powers of the LEDs with and without GMTL were measured to be 286.7 mW and 204.2 mW, respectively. As much as 40.4% increased light output power was achieved. Therefore, using the GMTL to reduce dislocation defects would be a promising prospective for InGaN/AlGaN UV LEDs to achieve high internal quantum efficiency.

Paper Details

Date Published: 27 February 2012
PDF: 7 pages
Proc. SPIE 8262, Gallium Nitride Materials and Devices VII, 82621L (27 February 2012); doi: 10.1117/12.909580
Show Author Affiliations
Shih-Cheng Huang, National Chung Hsing Univ. (Taiwan)
Advanced Optoelectronic Technology Inc. (Taiwan)
Kun-Ching Shen, National Chung Hsing Univ. (Taiwan)
Po-Min Tu, National Chiao Tung Univ. (Taiwan)
Dong-Sing Wuu, National Chung Hsing Univ. (Taiwan)
Da-Yeh Univ. (Taiwan)
Hao-Chung Kuo, National Chiao Tung Univ. (Taiwan)
Ray-Hua Horng, National Cheng Kung Univ. (Taiwan)


Published in SPIE Proceedings Vol. 8262:
Gallium Nitride Materials and Devices VII
Jen-Inn Chyi; Yasushi Nanishi; Hadis Morkoç; Joachim Piprek; Euijoon Yoon, Editor(s)

© SPIE. Terms of Use
Back to Top