Understanding microstructural effects on long term electrical fatigue in multilayer PZT actuators
Author(s): Jens Müller; Stephanie A. Hooker; Davor Balzar
Format Member Price Non-Member Price
PDF $17.00 $21.00

Paper Abstract

In this study, multilayered PbZrxTi1-xO3 (PZT) samples were produced by tape-casting and subsequent sintering at temperatures in the range of 1175 °C to 1325 °C. Sintering times were 6 minutes and 24 minutes. Samples were poled and also electrically fatigued by long-term exposure (≈106 cycles) to cyclic electric fields. The parameters of initial and remnant polarization were estimated from hysteresis loops. Changes in the crystallographic microstructure as a function of sintering temperature TS and sintering time were examined by scanning electron microscopy (SEM) and X-ray diffraction (XRD) to gain insight on fatigue mechanisms and their prevention. The microstructural results, such as domain reorientation and amount of secondary phases, explained the results of electrical observations. We found that grain sizes and internal strains were major influence factors on device performance. Domain sizes were about two orders of magnitude smaller than grain sizes. Therefore, domain-grain wall interaction did not influence domain switching. Domain wall movement was facilitated in samples processed at TS less than 1250 °C, and such samples were more resistant to electrical fatigue. Samples degraded faster at TS above 1250 °C, but here a higher device performance power was found due to an increased unit cell tetragonality that yielded higher polarization values.

Paper Details

Date Published: 6 April 2006
PDF: 8 pages
Proc. SPIE 6170, Smart Structures and Materials 2006: Active Materials: Behavior and Mechanics, 61700D (6 April 2006); doi: 10.1117/12.658847
Show Author Affiliations
Jens Müller, National Institute of Standards and Technology (United States)
Stephanie A. Hooker, National Institute of Standards and Technology (United States)
Davor Balzar, National Institute of Standards and Technology (United States)
Univ. of Denver (United States)

Published in SPIE Proceedings Vol. 6170:
Smart Structures and Materials 2006: Active Materials: Behavior and Mechanics
William D. Armstrong, Editor(s)

© SPIE. Terms of Use
Back to Top
Sign in to read the full article
Create a free SPIE account to get access to
premium articles and original research
Forgot your username?