Effect of deposition parameters on the stress gradient of CVD and PECVD poly-SiGe for MEMS applications
Author(s): Tom Van der Donck; Joris Proost; Cristina Rusu; Kris Baert; Chris Van Hoof; Jean-Pierre Celis; Ann Witvrouw
Format Member Price Non-Member Price
PDF $17.00 $21.00

Paper Abstract

The effect of the deposition parameters and Ge content on the stress gradient in poly-SiGe films was investigated. The films, ranging in thickness from 1.2 to 2.3 μm, were deposited by chemical vapor deposition (CVD) at 450 °C and plasma enhanced chemical vapor deposition (PECVD) at 520 °C. The Ge content was varied between 45 and 64 at%. Xray diffraction revealed that both PECVD and CVD films were polycrystalline. The stress gradient was determined by measuring the deflection of 1 mm long released cantilevers. The stress gradient was found to decrease with increasing Ge content. A CVD film with 55 at% Ge was thinned using a very low power SF6/O2 plasma. The stress gradient was measured as a function of film thickness. The stress profile was calculated by matching the bending moment of the calculated profile to the bending moment obtained from the measured stress gradient. The largest change in stress occurs right at the thin film/substrate interface. PECVD films were found to possess a lower stress gradient compared to CVD films with similar thickness. This was explained by differences in TEM microstructure: CVD films have more Vshaped grains, while PECVD films have more columnar grains.

Paper Details

Date Published: 30 December 2003
PDF: 11 pages
Proc. SPIE 5342, Micromachining and Microfabrication Process Technology IX, (30 December 2003); doi: 10.1117/12.524406
Show Author Affiliations
Tom Van der Donck, IMEC (Belgium)
Katholieke Univ. Leuven (Belgium)
Joris Proost, Katholieke Univ. Leuven (Belgium)
Cristina Rusu, IMEC (Belgium)
Kris Baert, IMEC (Belgium)
Chris Van Hoof, IMEC (Belgium)
Jean-Pierre Celis, Katholieke Univ. Leuven (Belgium)
Ann Witvrouw, IMEC (Belgium)

Published in SPIE Proceedings Vol. 5342:
Micromachining and Microfabrication Process Technology IX
Mary Ann Maher; Jerome F. Jakubczak, Editor(s)

© SPIE. Terms of Use
Back to Top
Sign in to read the full article
Create a free SPIE account to get access to
premium articles and original research
Forgot your username?