Modified ferroelectric properties of the single c-domain/single crystal PbTiO3 thin films with tightly bonded interface
Author(s): Kiyotaka Wasa; Ryuta Ai; Goh Asayama; Yoko Ichikawa; Hideaki Adachi
Format Member Price Non-Member Price
PDF $17.00 $21.00

Paper Abstract

Continuous single c-domain/single crystal thin films of PbTiO3 (PT), 10 to 300 nm in film thickness, were epitaxially grown on the miscut (001)SrTiO3 substrates. The PT thin films were grown under a step-flow growth and their surface was atomically flat. The interface between thin films and the substrates were coherent. These sputtered PT thin films were tetragonally deformed by the thin films were tightly bonded to the substrates. The lattice parameters did not change at the Curie temperature. The PT thin films exhibited modified ferroelectric properties and/or second order like ferro-paraelectric phase transition. The PT thin films exhibited a diffused peak at the Curie temperature of 520 degrees Celsius. The P/E hysteresis curve showed a sharp switching property with a rectangular pattern and a high coercive field of 400 to 500 kV/cm.

Paper Details

Date Published: 6 September 2000
PDF: 8 pages
Proc. SPIE 4058, Superconducting and Related Oxides: Physics and Nanoengineering IV, (6 September 2000); doi: 10.1117/12.397846
Show Author Affiliations
Kiyotaka Wasa, Yokohama City Univ. (Japan)
Ryuta Ai, Yokohama City Univ. (Japan)
Goh Asayama, Yokohama City Univ. (Japan)
Yoko Ichikawa, Research Institute of Innovative Technology for the Earth (Japan)
Hideaki Adachi, Matsushita Electric Co., Ltd. (Japan)


Published in SPIE Proceedings Vol. 4058:
Superconducting and Related Oxides: Physics and Nanoengineering IV
Davor Pavuna; Ivan Bozovic, Editor(s)

© SPIE. Terms of Use
Back to Top