Bond strength of composites on Er:YAG and Er,Cr:YSGG laser-irradiated enamel
Author(s): Christian Apel; Norbert Gutknecht
Format Member Price Non-Member Price
PDF $17.00 $21.00

Paper Abstract

In an in vitro study the bond strength of composite materials on Er:YAG and Er,Cr:YSGG laser-radiated enamel was examined. The results achieved on enamel surfaces conditioned conventionally using the acid etching method served as a control. On 80 extracted cariesfree third molars an enamel area of 4 X 4 mm was conditioned with three different systems. The Er:YAG laser was used at pulse frequencies of 8 Hz, 10 Hz, 12 Hz and 15 Hz using an energy of 120 mJ at each setting. The Er,Cr:YSGG laser was used at the settings of 20 Hz/50 mJ, 20 Hz/100 mJ and 20 Hz/150 mJ. The repetition rate for this device is constantly 20 Hz. In the reference group 10 teeth were etched with 37% phosphoric acid. In order to be able to perform the tensile tests under standard conditions metal brackets were placed on the conditioned surfaces. The 'Orthodontic-Bonding-System' was used as an adhesive system. The brackets were pulled off from the etched surfaces vertically to the tooth using a tensile testing machine. The results confirmed the highest bond strengths in the group of enamel surfaces which have been conditioned with acid etching gel. The bond strength of the Er:YAG laser (8, 10 and 12 Hz)- and Er,Cr:YSGG laser (20 Hz/150 mJ)-conditioned enamel surfaces was not significantly lower.

Paper Details

Date Published: 4 February 1999
PDF: 4 pages
Proc. SPIE 3564, Medical Applications of Lasers in Dermatology, Cardiology, Ophthalmology, and Dentistry II, (4 February 1999); doi: 10.1117/12.339156
Show Author Affiliations
Christian Apel, Univ. of Aachen Medical School (Germany)
Norbert Gutknecht, Univ. of Aachen Medical School (Germany)

Published in SPIE Proceedings Vol. 3564:
Medical Applications of Lasers in Dermatology, Cardiology, Ophthalmology, and Dentistry II
Gregory B. Altshuler; Stefan Andersson-Engels; Reginald Birngruber; Peter Bjerring; Adolf Friedrich Fercher; Herbert J. Geschwind M.D.; Raimund Hibst; Herbert Hoenigsmann; Frederic Laffitte; Hericus J. C. M. Sterenborg, Editor(s)

© SPIE. Terms of Use
Back to Top
Sign in to read the full article
Create a free SPIE account to get access to
premium articles and original research
Forgot your username?