Damage free Al doping on 4H-SiC with passivation films using XeF excimer laser irradiation in AlCl3 acid solution
Author(s): T. Tsuchiya; A. Suwa; A. Ikeda; D. Nakamura; T. Asano; H. Ikenoue
Format Member Price Non-Member Price
PDF $17.00 $21.00

Paper Abstract

We propose an innovative method for aluminum doping of 4H-SiC with passivation films, induced by XeF excimer laser irradiation in AlCl3 aqueous solution (28.6 wt%). A 100-nm thick Si passivation film was deposited on an n-type 4H-SiC substrate by physical vapor deposition. Using a laser beam (200 μm × 170 μm) with an irradiation fluence of 0.5–5.0 J/cm2, 1–300 shots were administered. After laser irradiation of 1.0 J/cm2 and 300 shots, an Al-Si-O compound film was formed on the SiC surface. The compound film was removed by chemical wet etching and plasma treatment. After the removal of the compound film, no irradiation damage was observed on the SiC surface. From the results of secondary ion mass spectrometry measurements, high concentration aluminum doping (about 1 × 1020 /cm3 at the surface) was confirmed. The I-V characteristics of the junction between the n-type substrate and the irradiation area indicated clear rectification with a large on/off ratio of 9 decades in the range of ±10 V. When forward biased, electroluminescence phenomenon with a peak at 387 nm, corresponding to the electroluminescence of SiC’s band gap, was confirmed. These results prove the achievement of Al doping of n-type SiC to p-type using laser irradiation without any damage to the SiC surface.

Paper Details

Date Published: 20 February 2017
PDF: 9 pages
Proc. SPIE 10091, Laser Applications in Microelectronic and Optoelectronic Manufacturing (LAMOM) XXII, 1009106 (20 February 2017); doi: 10.1117/12.2250712
Show Author Affiliations
T. Tsuchiya, Kyushu Univ. (Japan)
A. Suwa, Kyushu Univ. (Japan)
A. Ikeda, Kyushu Univ. (Japan)
D. Nakamura, Kyushu Univ. (Japan)
T. Asano, Kyushu Univ. (Japan)
H. Ikenoue, Kyushu Univ. (Japan)

Published in SPIE Proceedings Vol. 10091:
Laser Applications in Microelectronic and Optoelectronic Manufacturing (LAMOM) XXII
Beat Neuenschwander; Costas P. Grigoropoulos; Tetsuya Makimura; Gediminas Račiukaitis, Editor(s)

© SPIE. Terms of Use
Back to Top
Sign in to read the full article
Create a free SPIE account to get access to
premium articles and original research
Forgot your username?