Nanoparticles of layered GaSe, InSe were fabricated by laser ablation (LA) method (KrF laser, λ = 248 nm, 50 Hz, maximum energy 200 mJ, τ = 4 ns) and characterized by: •XRF; •GDOES; •SEM and TEM; •UV-, VIS-, and IRabsorption; •Raman and PL spectroscopy (also in confocal geometry). Results are discussed in relation to the particle size. Absorption spectra of particles with diameter 20 nm and less turned out to be blue shifted and is consisted with a weak confinement effect on Wannier-Mott type excitons. It is shown, that with decreasing the particle size the energy position of the low-frequency Raman active phonons in both compounds are shifted to lower frequencies (21 and 18 cm^-1 in bulk GaSe and InSe and 8 and 7 cm^-1 in particles with sizes 5 and 7 nm, respectively). From the low frequency Raman data, decrease of the force constants ca. 25 % (for GaSe) due to the formation of the nanoparticles are estimated, and the origin is suggested. Second harmonic generation (SHG) with 1064 nm line of a mode locked Nd : YAG laser was observed for nanoparticles ablated on different substrates. Potential for using these structures for laser light visualizators are discussed.

Date Published: 15 December 2015
PDF: 12 pages
Proc. SPIE 9810, International Conference on Atomic and Molecular Pulsed Lasers XII, 981017 (15 December 2015); doi: 10.1117/12.2225218

Published in SPIE Proceedings Vol. 9810:
International Conference on Atomic and Molecular Pulsed Lasers XII
Victor F. Tarasenko; Andrey M. Kabanov; Andrey M. Kabanov, Editor(s)