Use of scanning thickness mapping technique to perform precision measurements of thin film thickness
Author(s): Richard G. Sartore
Format Member Price Non-Member Price
PDF $17.00 $21.00

Paper Abstract

By means of electron-beam induced x-rays, the thickness of films used in fabrication of integrated circuits can be measured with high precision. The thickness modulated intensity of the x-rays generated from the sub-layer material due to penetration of the electron beam is correlated to the thickness of the surface film and displayed as a 3-D thickness map of the film material)'2 Scanning thickness mapping is a technique for measuring and plotting film thickness over the surface of the devices with high spatial resolution in the X-Y plane, using the modulation effect on electron beam induced x-rays. This technique has been implemented at this laboratory using a scanning electron microscope (SEM) in conjunction with an energy dispersive x-ray analyzer (EDXA). Since the electrons must interact with the material below the film that is being measured, they must be of sufficient energy to penetrate the film and produce enough x-rays in the sub-layer to be detectable in a reasonable time frame. To accomplish this, the analyst is required to initially determine the optimum beam energy for the sample to be measured. Typically, the optimum beam energy is several kilovolts above the onset of beam penetration through the film. This report will present data obtained for a dielectric film over aluminum metal and aluminum on silicon. A simulated 3-D scanning thickness mapping display of dielectric thickness was obtained by converting raw x-ray intensity data received from the energy dispersive x-ray analyzer. The raw x-ray intensity data was corrected for x-ray absorption effects and translated into film thickness values. These calculated values were then compared to SEM visual measurements of a cross-sectioned sample. Correlation between the scanning thickness mapping measurements and the SEM visual measurements will be discussed. The benefits of this technique are the high degree of characterization of the film thickness in the X-Y plane, and the detection of hole defects in film and thickness non-uniformities at contact areas or at steps.

Paper Details

Date Published: 1 June 1990
PDF: 12 pages
Proc. SPIE 1261, Integrated Circuit Metrology, Inspection, and Process Control IV, (1 June 1990); doi: 10.1117/12.20029
Show Author Affiliations
Richard G. Sartore, U.S. Army Electronics Technolo (United States)

Published in SPIE Proceedings Vol. 1261:
Integrated Circuit Metrology, Inspection, and Process Control IV
William H. Arnold, Editor(s)

© SPIE. Terms of Use
Back to Top
Sign in to read the full article
Create a free SPIE account to get access to
premium articles and original research
Forgot your username?