YBa2Cu3O7-x -YxPr1-xBa2Cu3O7-x Heterostructures For Alga Temperature Superconductive Electronics
Author(s): C. T. Rogers; A. Inam; T. Venkatesan
Format Member Price Non-Member Price
PDF $14.40 $18.00
cover GOOD NEWS! Your organization subscribes to the SPIE Digital Library. You may be able to download this paper for free. Check Access

Paper Abstract

Many of the applications envisioned for the high temperature superconductors (HTSC) lie in the area of Josephson electronics, but realization of this technological promise requires a controllable multi-layer process which would admit the possibility of insulating layers, useful for applications from ground-plane isolation to tunnel-barrier formation, in combination with high quality superconducting or normal-conducting layers. We have begun investigating the growth and processing techniques necessary to realize these structures by studying a prototype multi-layer system based on Y Pr1-xBa2Cu307-x alloys. This class of materials is of great interest due to two facts: By varying the Pr concentration, x, the material's resistivity can be tuned. For x=0, we have pure YBa2Cu307-x (YBCO) which is a 90K superconductor; with increasing x, Tc decreases until at x =1 with pure PrBa2Cu307_ (PBCO) we find a divergent resistivity with decreasing T. Secondly, over the full alloy range, 0<x <1, the material remains orthorhombic in structure and is lattice matched to YBCO to a fraction of a percent. 1 Our major effort to date has been to study Josephson weak-link formation by using YBCO for electrodes and PBCO as a lattice-matched semiconducting barrier layer. 2 The first step is the growth of a heteroepitaxial four-layer structure of YBCO - PBCO YBCO - Au, using our standard laser deposition process. "All layers are grown during a single cycle of the vacuum system. We use Rutherford backscattering, both in the random and channeling modes, and X-ray scattering to verify layer stoichometry and heteroepitaxial growth of the orthorhombic perovskite structure, c-axis normal to the substrate. Both YBCO layers have sharp superconducting transitions above 80K upon removal from the vacuum system. Single devices with areas, A, from 2.5x10-5cm2 to 2x10-7crn2 are isolated with a four-step fabrication procedure involving standard photolithography and Ar ion milling. These devices show Current-Voltage characteristics similar to those observed for low temperature Superconductor /Normal metal /Superconductor (SNS) devices. We find good scaling of the critical currents. I. with A and scaling of the resistances, R7, with 1/A; the typical values of the /c.R7 product of 3.5rnV are consistent with traditional SNS behavior. Further, we observe Shapiro steps in response to 100GHz mm-wave radiation and oscillation of the d.c. supercurrent in a transverse magnetic field thus demonstrating that both the a.c. and d.c. Josephson effect occurs in these devices. These preliminary results suggest that our multi-layer process can be optimized for a variety of Josephson devices essential in producing electronic circuitry from the HTSC systems.

Paper Details

Date Published: 19 March 1990
PDF: 1 pages
Proc. SPIE 1187, Processing of Films for High Tc Superconducting Electronics, (19 March 1990); doi: 10.1117/12.965174
Show Author Affiliations
C. T. Rogers, Bellcore (United States)
A. Inam, Bellcore (United States)
T. Venkatesan, Bellcore (United States)

Published in SPIE Proceedings Vol. 1187:
Processing of Films for High Tc Superconducting Electronics
T. Venkatesan, Editor(s)

© SPIE. Terms of Use
Back to Top