Synthesis And Lithographic Characterization Of A Novel Organosilicon Novolac Resin
Author(s): Regine G. Tarascon; Ann Shugard; Elsa Reichmanis
Format Member Price Non-Member Price
PDF $14.40 $18.00
cover GOOD NEWS! Your organization subscribes to the SPIE Digital Library. You may be able to download this paper for free. Check Access

Paper Abstract

A novel terpolymer of a methylated phenol, p-trimethylsilylmethyl phenol and formaldehyde was synthesized. With a 9.7wt% Si content, the polymer displayed an RIE resistance 10 times greater than hard-baked HPR 204. The organosilicon novolac was employed as a base resin component of bilevel resist systems for both photo and electron-beam lithography. The low molecular weight polymer behaves as a positive resist when mixed with a dissolution inhibitor. In photo-lithography, the dissolution inhibitor was a diazoquinone based chemical which was converted to an acidic species during irradiation. In electron-beam lithography, poly (2-methyl-l-pentene sulfone) (PMPS), which depolymerizes upon electron-irradiation, functioned as the dissolution inhibitor. When the silylated novolac was used as a photoresist, coded 0.8μm line/space patterns were obtained with a sensitivity of -120 mJ/cm2. When employed as,an electron-beam resist coded 0.75μm line/space patterns were resolved with a dose of 8μC/cm4.

Paper Details

Date Published: 9 July 1986
PDF: 8 pages
Proc. SPIE 0631, Advances in Resist Technology and Processing III, (9 July 1986); doi: 10.1117/12.963624
Show Author Affiliations
Regine G. Tarascon, AT&T Bell Laboratories (United States)
Ann Shugard, AT&T Bell Laboratories (United States)
Elsa Reichmanis, AT&T Bell Laboratories (United States)


Published in SPIE Proceedings Vol. 0631:
Advances in Resist Technology and Processing III
C. Grant Willson, Editor(s)

© SPIE. Terms of Use
Back to Top