Adhesion Of Chromium Films To Various Glasses Used In Photomasks
Author(s): Yuji Nakajima; Tetsuro lzumitani; Yasuo Fukuoka
Format Member Price Non-Member Price
PDF $14.40 $18.00

Paper Abstract

The adhesion of chromium films to various glass substrates has been studied in various glass composition. 16 types of glasses were prepared by substituting B2O3 for SiO2, Al203 for CaO, and RO and R2O for CaO respectively in an almino-silicate glass. The adhesion of chromium films is evaluated by the so-called "scratch test" and observation of pinholes generated by ultrasonic agitation. It was found that a) with increased content of B2O3, pinhole density, ρ, increased and critical load Wc, at which film was stripped from substrate by scratching, decreased, b) with substitution of RO for CaO, ρ became larger in the order of CaO < MgO, ZnO < SrO, BaO, PbO, and Wc decreased in the order of MgO > CaO > ZnO > SrO, BaO, PbO, c) with R2O3 substitution, ρ decreased in the order of K2O, Na2O, Li2O. Thus, it is clear that B2O3, BaO, SrO, PbO, K2O and Na2O in glass contribute to poor adhesion of chromium films. It was also fauna that HOYA LE-30 glass had excellent adhesion to exceed an ordinary alumino-boro-silicate glass.

Paper Details

Date Published: 6 September 1978
PDF: 5 pages
Proc. SPIE 0135, Developments in Semiconductor Microlithography III, (6 September 1978); doi: 10.1117/12.956127
Show Author Affiliations
Yuji Nakajima, Hoya Corporation (Japan)
Tetsuro lzumitani, Hoya Corporation (Japan)
Yasuo Fukuoka, Hoya Corporation (Japan)


Published in SPIE Proceedings Vol. 0135:
Developments in Semiconductor Microlithography III
Dino R. Ciarlo; James W. Dey; Ken Hoeppner, Editor(s)

© SPIE. Terms of Use
Back to Top