Vibrational Properties Of Rf Sputtered Hydrogenated Amorphous Ge-Si Alloys
Author(s): D. K. Paul; P. K. Banerjee; R. Dutta; S. S. Mitra
Format Member Price Non-Member Price
PDF $14.40 $18.00

Paper Abstract

Amorphous Ge-SisH alloys have been prepared by r.f. sputtering in an argon-hydrogen atmosphere of varying hydrogen partial pressure and substrate temperature. The correlated data of the vibrational properties as measured by IR absorption and Raman scattering on these samples reveal several hydrogenic and lattice modes. The hydrogenic modes which grow with increasing hydrogenation can be identified with various Ge (Si)-H type molecular modes. The absorption due to Si-H modes appears stronger than that due to Ge-H modes, indicating a pre-ferential H attachment to Si atoms. Dehydrogenation by annealing at successively high temperatures leads to selective reduction/disappearance of certain modes assigned to Ge (Si)-H vibrations. Also, the observed variation (0.1 to 0.7) in the depolarisation ratio for the Raman spectra of asdeposited samples become stabilised at 0.5 with annealing. These data are interpreted in terms of the film growth process and associated structural inhomogeneities and H- bonding configurations.

Paper Details

Date Published: 15 September 1982
PDF: 7 pages
Proc. SPIE 0346, Thin Film Technologies and Special Applications, (15 September 1982); doi: 10.1117/12.933798
Show Author Affiliations
D. K. Paul, Harvard University (United States)
P. K. Banerjee, University of Rhode Island (United States)
R. Dutta, University of Rhode Island (United States)
S. S. Mitra, University of Rhode Island (United States)


Published in SPIE Proceedings Vol. 0346:
Thin Film Technologies and Special Applications
William R. Hunter, Editor(s)

© SPIE. Terms of Use
Back to Top