Scaling of GaN single nanowire MOSFET with cut-off frequency 150GHz
Author(s): Jeng-Wei Yu; Yuh-Renn Wu; Lung-Han Peng
Format Member Price Non-Member Price
PDF $14.40 $18.00

Paper Abstract

We characterize the transport properties of [11-20] GaN/Ga2O3 nanowire (NW)-MOSFET epitaxially grown on (0001) sapphire substrates. When passivated with 10nm-thick Ga2O3 on the {1-10-1 }GaN triangular facets, the 50 nm-dia. Ga2O3/GaN NW-MOSFET with 50nm gate length exhibits a saturation current of 130 μA, transconductance of 64 μS, current on/off ratio of 104, subthreshold swing of 100mV/dec, and unity current (power) gain bandwidth fT (fMAX) at 150 (180)GHz. Using a 3D diffusion and drift model analysis, we found that the short channel effect in a Lg=50nm Ga2O3/GaN NW-MOSFET at an aspect ratio of 5 was suppressed due to contribution from polarization-induced negative space charge of -2.8×1012 cm2 at the abrupt crystalline interface between GaN NW and sapphire. The superior DC transport properties and good RF response can be ascribed the to polarization-induced 2D electron gas (2DEG) density of 7× 1012 cm2 with mobility of 1000cm2/V-sec confined at the semi-polar {1-10-1} GaN/Ga2O3 interfaces.

Paper Details

Date Published: 27 February 2012
PDF: 6 pages
Proc. SPIE 8262, Gallium Nitride Materials and Devices VII, 82620N (27 February 2012); doi: 10.1117/12.912041
Show Author Affiliations
Jeng-Wei Yu, National Taiwan Univ. (Taiwan)
Yuh-Renn Wu, National Taiwan Univ. (Taiwan)
Lung-Han Peng, National Taiwan Univ. (Taiwan)


Published in SPIE Proceedings Vol. 8262:
Gallium Nitride Materials and Devices VII
Jen-Inn Chyi; Yasushi Nanishi; Hadis Morkoç; Joachim Piprek; Euijoon Yoon, Editor(s)

© SPIE. Terms of Use
Back to Top