Structural and optical properties of a-plane GaN on r-plane sapphire with titanium oxide nanoparticles coated by spin coating method
Author(s): Ji Hoon Kim; Jung Ho Park; Kwang Hyeon Baik; Sung-Min Hwang
Format Member Price Non-Member Price
PDF $14.40 $18.00

Paper Abstract

We investigated the structural and optical characteristics of nonpolar a-plane (11-20) GaN structure grown on TiO2 nanoparticles (NP)-coated r-plane sapphire by spin coating method. The surface morphology without any observable inverse pyramidal pits was observed by atomic force microscopy (AFM) measurement. Transmission electron microscopy (TEM) analysis revealed that the threading dislocations (TDs) and basal plane stacking faults (BSFs) densities were around 4.5 × 109 cm-2 and 3.1 × 105 cm-1, respectively. It was also found that the broadening of x-ray rocking curves (XRC) full width at a half maximum (FWHM) in Si-doped a-plane GaN on the TiO2 NP-coated r-plane sapphire was affected by the tilt and twist of mosaic crystals. The photoluminescence (PL) intensity of TiO2 NP-related MQWs sample at 295 K was approximately 18 % higher than that of the reference sample. This implied that the improved PL intensity was attributed to scattering of light by TiO2 NP and InGaN/GaN MQWs interface of high quality.

Paper Details

Date Published: 17 September 2011
PDF: 7 pages
Proc. SPIE 8123, Eleventh International Conference on Solid State Lighting, 812314 (17 September 2011); doi: 10.1117/12.893321
Show Author Affiliations
Ji Hoon Kim, Korea Univ. (Korea, Republic of)
Korea Electronics Technology Institute (Korea, Republic of)
Jung Ho Park, Korea Univ. (Korea, Republic of)
Kwang Hyeon Baik, Korea Electronics Technology Institute (Korea, Republic of)
Sung-Min Hwang, Korea Electronics Technology Institute (Korea, Republic of)


Published in SPIE Proceedings Vol. 8123:
Eleventh International Conference on Solid State Lighting
Matthew H. Kane; Christian Wetzel; Jian-Jang Huang, Editor(s)

© SPIE. Terms of Use
Back to Top