New materials for uncooled IR imaging: nickel manganite thin films grown by spin spray
Author(s): Song Won Ko; Jing Li; Myung-Yoon Lee; Elizabeth Dickey; Thomas Jackson; Susan Trollier-McKinstry
Format Member Price Non-Member Price
PDF $14.40 $18.00
cover GOOD NEWS! Your organization subscribes to the SPIE Digital Library. You may be able to download this paper for free. Check Access

Paper Abstract

Ceramic thermistors like VOx, amorphous Si, and NiMn2O4 are used for thermal sensing applications such as microbolometers and infrared sensors. These materials should have large temperature coefficient of resistance (TCR), high sensitivity, and low noise for these applications. Nickel manganite films have large TCR (>-3%/K) and good environmental stability, so that the properties are robust during subsequent processing. To improve the ability to prepare manganite spinels on pre-existing circuitry, new techniques that enable low-temperature depositions need to be developed. To address this, the spin spray technique was adopted in this work; this approach is both low cost and permits low process temperatures (<100oC). Spin spray deposition is accomplished using two dilute water-based solutions: a reaction solution and oxidizing solution. The reaction solution consists of metal salts like nickel chloride and manganese chloride while the oxidizing solution contains pH buffer, pH adjuster, and oxidizing agent. To grow films, the solution was nebulized by a nitrogen carrier gas and sprayed onto a rotating silicon substrate with a 1μm thick SiO2 buffer layer. As-deposited nickel manganite films were identified as nanocrystalline spinel by TEM analysis. The TCR values of nickel manganite film and nickel copper manganite film were about -3.6 %/K and -2.9 %/K respectively. Adding Cu allowed the electric resistivity to be tuned to less than 1000 Ω-cm. The normalized Hooge parameter was around 1.7x10- 21 cm3.

Paper Details

Date Published: 21 May 2011
PDF: 5 pages
Proc. SPIE 8012, Infrared Technology and Applications XXXVII, 80123S (21 May 2011); doi: 10.1117/12.884636
Show Author Affiliations
Song Won Ko, The Pennsylvania State Univ. (United States)
Jing Li, The Pennsylvania State Univ. (United States)
Myung-Yoon Lee, The Pennsylvania State Univ. (United States)
Elizabeth Dickey, North Carolina State Univ. (United States)
Thomas Jackson, The Pennsylvania State Univ. (United States)
Susan Trollier-McKinstry, The Pennsylvania State Univ. (United States)


Published in SPIE Proceedings Vol. 8012:
Infrared Technology and Applications XXXVII
Bjørn F. Andresen; Gabor F. Fulop; Paul R. Norton, Editor(s)

© SPIE. Terms of Use
Back to Top