Wafer-edge defect reduction for tri-layer materials in BEOL applications
Author(s): J. R. Du; C. H. Huang; Elvis Yang; T. H. Yang; K. C. Chen; Chih-Yuan Lu
Format Member Price Non-Member Price
PDF $14.40 $18.00
cover GOOD NEWS! Your organization subscribes to the SPIE Digital Library. You may be able to download this paper for free. Check Access

Paper Abstract

As the semiconductor feature size continues to shrink, the thickness of photo resist needs to be thinner and thinner to prevent resist features from collapse. Coupling with the need of high NA lithography for small feature patterning, both the reflectance control and the etch budget on resist thickness are becoming major challenges for lithographers. One way to simultaneously satisfy the needs of superior low reflectance, sufficient etch resistance and minimizing the resist feature collapse is adopting tri-layer lithography scheme. The tri-layer scheme has been successfully implemented in our manufacturing flow for FEOL (Front-End-of-Line) application. This work investigated the application of tri-layer scheme to BEOL (Back-End-of-Line) AlCu patterning. One critical problem met in this application is the defect that majorly originates from wafer edge after AlCu patterning. The defects were finally ascribed to the hump formation of Si-rich hard-mask by EBR (Edge Bead Removal) process. The hump of Si-rich hard-mask yields etch masking behavior during AlCu etch accordingly leads to pattern bridging or peeling of inorganic hard-mask after AlCu patterning. To reduce the defect, several evaluations were made to suppress the hump formation, including the EBR optimization, bake condition of Si-rich hard-mask, film stacking architecture of tri-layer by EBR rinse and surfactant additive added Si-rich hard-mask. A synergy effect among process factors has been proposed to effectively fix the defect problem around wafer edge.

Paper Details

Date Published: 20 April 2011
PDF: 10 pages
Proc. SPIE 7971, Metrology, Inspection, and Process Control for Microlithography XXV, 79712L (20 April 2011); doi: 10.1117/12.879191
Show Author Affiliations
J. R. Du, Macronix International Co., Ltd. (Taiwan)
C. H. Huang, Macronix International Co., Ltd. (Taiwan)
Elvis Yang, Macronix International Co., Ltd (Taiwan)
T. H. Yang, Macronix International Co., Ltd (Taiwan)
K. C. Chen, Macronix International Co., Ltd (Taiwan)
Chih-Yuan Lu, Macronix International Co., Ltd (Taiwan)


Published in SPIE Proceedings Vol. 7971:
Metrology, Inspection, and Process Control for Microlithography XXV
Christopher J. Raymond, Editor(s)

© SPIE. Terms of Use
Back to Top