Plasma pre-treatment effect for photo-oxidized coating and adhesion to optical glass surface
Author(s): Yuji Sato; Masataka Murahara; Takahisa Jitsuno; Yoshiaki Okamoto
Format Member Price Non-Member Price
PDF $14.40 $18.00
cover GOOD NEWS! Your organization subscribes to the SPIE Digital Library. You may be able to download this paper for free. Check Access

Paper Abstract

There is the method to form microscopic roughness on the surface of a sample in order that a film or adhesive is hard to peel off, but it is unsuitable to optical material surfaces. We, thus, demonstrated the undamaged surface of the optical material on which the coating agent or adhesive was applied by chemically incorporating the functional groups. Many thin films are deposited, but most of them come off if wiped. Then, hydrophilic groups (-OH) were incorporated on the sample surface beforehand, and photo-adhesion or coating was carried out. The sample surface was firstly treated by discharge plasma for promoting efficiency of hydroxyl group substitution, and hydroxyl groups were incorporated on the modified side in water ambient when the material temporarily maintained high wettability; as a result, the adhesion or coating and the modified side were united persistently. The contact angle with water of fused silica is 40 degrees; that of sapphire is 72 degrees; that of BK7 glass is 31 degrees. When those surfaces were irradiated by glow discharge plasma of DC pole sputtering system for five minutes, all of the surfaces dropped to five degrees. Under this condition, silicone oil was applied on each pretreated sample surface and irradiated with excimer lamp light (172nm) for 60 minutes. The adhesive strength of the silica glass plates with plasma pretreatment improved to 25M pascal when compared with that of the silica glass plates without pretreatment, which was 18M paschal.

Paper Details

Date Published: 6 December 2010
PDF: 6 pages
Proc. SPIE 7842, Laser-Induced Damage in Optical Materials: 2010, 784224 (6 December 2010); doi: 10.1117/12.867860
Show Author Affiliations
Yuji Sato, Tokyo Institute of Technology (Japan)
Masataka Murahara, Tokyo Institute of Technology (Japan)
Tokai Univ. (Japan)
Takahisa Jitsuno, Osaka Univ. (Japan)
Yoshiaki Okamoto, Okamoto Optics Co., Ltd. (Japan)


Published in SPIE Proceedings Vol. 7842:
Laser-Induced Damage in Optical Materials: 2010
Gregory J. Exarhos; Vitaly E. Gruzdev; Joseph A. Menapace; Detlev Ristau; M. J. Soileau, Editor(s)

© SPIE. Terms of Use
Back to Top