Author(s): Jie Lu; Guang-ping Zou
Format Member Price Non-Member Price
PDF $14.40 $18.00
cover GOOD NEWS! Your organization subscribes to the SPIE Digital Library. You may be able to download this paper for free. Check Access

Paper Abstract

The aim of this paper is to present a novel inertia moment algorithm meanwhile use it to investigate the stress corrosion initiation stage of an aluminum alloy. The specimens are Al-2A12 alloy with thickness of 2mm which are immersed in the 3.5% sodium chloride solution. Three-point bending system is employed under displacement loading mode. The center displacement is 2mm, 2.5mm and 4mm, respectively. Meanwhile in order to observe the stress corrosion process, the solution temperature increases from 20.9 to 61.3 degrees centigrade. Average intensity method is recommended to contrast due to its validity for corrosion analysis. The results show at room temperature, the material is not prone to stress corrosion. General electrochemical corrosion is a major role and the process is comparatively moderate. Stress corrosion appears when the temperature has increased. It is a phenomenon of localized corrosion and exhibits asymmetric property. Accompanied with the corrosion process developed, this kind of asymmetric property is increasingly apparent from three-dimensional results.

Paper Details

Date Published: 14 April 2010
PDF: 9 pages
Proc. SPIE 7522, Fourth International Conference on Experimental Mechanics, 75225E (14 April 2010); doi: 10.1117/12.851445
Show Author Affiliations
Jie Lu, Harbin Engineering Univ. (China)
Guang-ping Zou, Harbin Engineering Univ. (China)

Published in SPIE Proceedings Vol. 7522:
Fourth International Conference on Experimental Mechanics
Chenggen Quan; Kemao Qian; Anand Krishna Asundi; Fook Siong Chau, Editor(s)

© SPIE. Terms of Use
Back to Top