Uncooled SWIR InGaAs/GaAsSb type-II quantum well focal plane array
Author(s): H. Inada; K. Miura; H. Mori; Y. Nagai; Y. Iguchi; Y. Kawamura
Format Member Price Non-Member Price
PDF $14.40 $18.00
cover GOOD NEWS! Your organization subscribes to the SPIE Digital Library. You may be able to download this paper for free. Check Access

Paper Abstract

Low dark current photodiodes (PDs) in the short wavelength infrared (SWIR) upto 2.5μm region, are expected for many applications. HgCdTe (MCT) is predominantly used for infrared imaging applications. However, because of high dark current, MCT device requires a refrigerator such as stirling cooler, which increases power consumption, size and cost of the sensing system. Recently, InGaAs/GaAsSb type II quantum well structures were considered as attractive material system for realizing low dark current PDs owing to lattice-matching to InP substrate. Planar type PIN-PDs were successfully fabricated. The absorption layer with 250 pair-InGaAs(5nm)/GaAsSb(5nm) quantum well structures was grown on S-doped (100) InP substrates by solid source molecular beam epitaxy method. InP and InGaAs were used for cap layer and buffer layer, respectively. The p-n junctions were formed in the absorption layer by the selective diffusion of zinc. Diameter of light-receiving region was 140μm. Low dark current was obtained by improving GaAsSb crystalline quality. Dark current density was 0.92mA/cm2 which was smaller than that of a conventional MCT. Based on the same process as the discrete device, a 320x256 planar type focal plane array was also fabricated. Each PD has 15μm diameter and 30μm pitch and it was bonded to read-out IC by using indium bump flip chip process. Finally, we have successfully demonstrated the 320 x256 SWIR image at room temperature. This result means that planer type PD array with the type II InGaAs/GaAsSb quantum well structure is a promising candidate for uncooled applications.

Paper Details

Date Published: 3 May 2010
PDF: 7 pages
Proc. SPIE 7660, Infrared Technology and Applications XXXVI, 76603N (3 May 2010); doi: 10.1117/12.850590
Show Author Affiliations
H. Inada, Sumitomo Electric Industries, Ltd. (Japan)
K. Miura, Sumitomo Electric Industries, Ltd. (Japan)
H. Mori, Sumitomo Electric Industries, Ltd. (Japan)
Y. Nagai, Sumitomo Electric Industries, Ltd. (Japan)
Y. Iguchi, Sumitomo Electric Industries, Ltd. (Japan)
Y. Kawamura, Osaka Prefecture Univ. (Japan)


Published in SPIE Proceedings Vol. 7660:
Infrared Technology and Applications XXXVI
Bjørn F. Andresen; Gabor F. Fulop; Paul R. Norton, Editor(s)

© SPIE. Terms of Use
Back to Top