Chromium-doped zinc selenide gain media: from synthesis to pulsed mid-infrared laser operation
Author(s): A. Sennaroglu; U. Demirbas; H. Cankaya; N. Cizmeciyan; A. Kurt; M. Somer
Format Member Price Non-Member Price
PDF $14.40 $18.00

Paper Abstract

This paper provides an overview of the experimental work performed in our research group on the synthesis, spectroscopic investigation, and laser characterization of chromium-doped zinc selenide (Cr2+:ZnSe). By using diffusion doping, 40 polycrystalline Cr2+:ZnSe samples with ion concentration in the range of 0.8 × 1018 to 66 × 1018ions/cm3 were prepared. From the absorption data, temperature-dependent diffusion coefficient of chromium and losses at the lasing wavelength were measured. In luminescence measurements, the concentration dependence of the fluorescence lifetime and fluorescence quantum efficiency was determined. During continuous-wave operation, the optimum concentration for lasing was determined to be 8.5 × 1018 ions/cm3 at an incident pump power of 2.1 W for 1800-nm pumping. During gain switched operation, intra-cavity pumping with a 1570-nm optical parametric oscillator resulted in continuous tuning between 1880 and 3100 nm. By employing dispersion compensation with a MgF2 prism pair, Kerr-lens mode-locked operation was also demonstrated at 2420 nm, resulting in the generation of 95-fs pulses with an average output power of 40 mW and spectral bandwidth of 69 nm. The time-bandwidth product of the pulses was further measured to be 0.335 close to the expected value of 0.315 for sech2 pulses.

Paper Details

Date Published: 25 February 2010
PDF: 10 pages
Proc. SPIE 7598, Optical Components and Materials VII, 75981B (25 February 2010); doi: 10.1117/12.847098
Show Author Affiliations
A. Sennaroglu, Koç Univ. (Turkey)
U. Demirbas, Koç Univ. (Turkey)
Massachusetts Institute of Technology (United States)
H. Cankaya, Koç Univ. (Turkey)
N. Cizmeciyan, Koç Univ. (Turkey)
A. Kurt, Teknofil, Inc. (Turkey)
M. Somer, Koç Univ. (Turkey)

Published in SPIE Proceedings Vol. 7598:
Optical Components and Materials VII
Shibin Jiang; Michel J. F. Digonnet; John W. Glesener; J. Christopher Dries, Editor(s)

© SPIE. Terms of Use
Back to Top