Preparation and photoluminescence properties of porous silicon
Author(s): Zhiwei Chen; Zhimou Xu
Format Member Price Non-Member Price
PDF $14.40 $18.00
cover GOOD NEWS! Your organization subscribes to the SPIE Digital Library. You may be able to download this paper for free. Check Access

Paper Abstract

There are many preparation methods of porous silicon(PS), such as electrochemical etching(ECE), photochemical etching, chemical etching and so on. ECE, also known as anodic etching, is more common among these methods. A lot of holes are given priority to be etched on the surface of silicon. The top and vertical aspects of the holes are easily etched while horizontal aspects wall of the holes are quiet different, and then tree-like or sponge-like porous structure is formed. In this paper, we obtained porous structure on the surface of silicon using lithography and dry etching method. The diameter of the hole was 2μm or 6μm. The etching depth of the samples was about 70nm, 140nm and 260nm. Photoluminescence (PL) phenomenon was observed by using light of 270nm, 280nm, 330nm, 455nm and 460nm wavelength to excite the samples. The results showed that PL intensity was the best when excitation wavelength was 270nm or 280nm, compared with 330nm, 455nm and 460nm. From PL analysis of all samples, It exists three emission peaks about at 372nm, 425nm and 473nm. When the diameter of the PS was the same, it was found that PS with etching depth at 140nm was more efficient. It means that PL intensity of the was better than other samples when the etching depth was 140nm. Likewise, samples of which the diameter was 2μm has much better PL than that of the other samples.

Paper Details

Date Published: 28 October 2009
PDF: 7 pages
Proc. SPIE 7514, Photonics and Optoelectronics Meetings (POEM) 2009: Fiber Optic Communication and Sensors, 75140T (28 October 2009); doi: 10.1117/12.843427
Show Author Affiliations
Zhiwei Chen, Wuhan National Lab. for Optoelectronics (China)
Huazhong Univ. of Science and Technology (China)
Zhimou Xu, Wuhan National Lab. for Optoelectronics (China)
Huazhong Univ. of Science and Technology (China)


Published in SPIE Proceedings Vol. 7514:
Photonics and Optoelectronics Meetings (POEM) 2009: Fiber Optic Communication and Sensors
Dieter Stefan Jäger; Hequan Wu; Shuisheng Jian; Desheng Jiang; Deming Liu; Weiwei Dong; Qizhen Sun; Xiaochun Xiao, Editor(s)

© SPIE. Terms of Use
Back to Top