Mechanical behaviors of molded pulp material
Author(s): Hongwei Ji; Huaiwen Wang; Jinlong Chen
Format Member Price Non-Member Price
PDF $14.40 $18.00
cover GOOD NEWS! Your organization subscribes to the SPIE Digital Library. You may be able to download this paper for free. Check Access

Paper Abstract

Many mechanical phenomena of interest for web-like materials, such as molded pulp, take place at the micro-scale. A SEM (scanning electron microscope) with SHIMADZU electrohydraulic servo experimental system was employed to study the micro-scale mechanical behavior of molded pulp materials. Uniaxial tension tests of molded pulp specimens were carried out, resulting in the stress-strain curves. Experimental results indicated that the material is not only elasticplastic, but also emplastic. The surface morphology evolution of the tensile specimen was visually monitored during the process of loading, and some SEM micrographs were captured under different load levels. Full-field deformations over an area of 190x170 μm2 were obtained using the digital image correlation method. The higher strains occurred at the fibre fines zone or around voids whereas the lower strains were obviously found at long fibres, demonstrating that the strain distribution is obviously uneven. The reason may be due to the random orientation and the fraction of the fibres, and the presence of impurities and voids as well.

Paper Details

Date Published: 25 August 2009
PDF: 5 pages
Proc. SPIE 7375, ICEM 2008: International Conference on Experimental Mechanics 2008, 73756D (25 August 2009); doi: 10.1117/12.839376
Show Author Affiliations
Hongwei Ji, Tianjin Univ. of Commerce (China)
Huaiwen Wang, Tianjin Univ. of Commerce (China)
Jinlong Chen, Tianjin Univ. (China)

Published in SPIE Proceedings Vol. 7375:
ICEM 2008: International Conference on Experimental Mechanics 2008
Xiaoyuan He; Huimin Xie; YiLan Kang, Editor(s)

© SPIE. Terms of Use
Back to Top