Effect of resist polymer molecular weight on EUV lithography
Format Member Price Non-Member Price
PDF $14.40 $18.00
cover GOOD NEWS! Your organization subscribes to the SPIE Digital Library. You may be able to download this paper for free. Check Access

Paper Abstract

EUV lithography performances of resist materials with different molecular weight of polymer were investigated. EUV exposure experiment using a SFET at Selete clearly showed that line-width roughness (LWR) and 1:1 half-pitch (hp) resolution were each improved using the polymers with middle and low molecular weights. These polymers showed high dissolution contrast relative to polymer with high molecular weight. Mask linearity data also showed that the polymer with low molecular weight gave a linear dependence on critical dimension (CD) against mask size down to hp 26 nm. Thermal analysis of resist film revealed that thermal glass transition temperature (Tg) was dramatically decreased from 190 °C to 110 °C with decreasing molecular weight from high to low. In contrast with Tg which directly reflects mobility of polymer, exposure latitude (EL) was increased from 12.3% to 14.5% at hp 32 nm by decreasing molecular weight of polymer. Similarly, iso-dense bias was also improved by utilizing the low molecular weight polymer. Combination of PAG-B with the low molecular weight polymer caused further improvement in mask linearity, EL, and iso-dense bias at hp 32 nm, although LWR was rather increased.

Paper Details

Date Published: 1 April 2009
PDF: 10 pages
Proc. SPIE 7273, Advances in Resist Materials and Processing Technology XXVI, 72733S (1 April 2009); doi: 10.1117/12.812204
Show Author Affiliations
Hideaki Tsubaki, FUJIFILM Co., Ltd (Japan)
Katsuhiro Yamashita, FUJIFILM Co., Ltd (Japan)
Hidenori Takahashi, FUJIFILM Co., Ltd (Japan)
Daisuke Kawamura, Semiconductor Leading Edge Technologies, Inc. (Japan)
Toshiro Itani, Semiconductor Leading Edge Technologies, Inc. (Japan)


Published in SPIE Proceedings Vol. 7273:
Advances in Resist Materials and Processing Technology XXVI
Clifford L. Henderson, Editor(s)

© SPIE. Terms of Use
Back to Top