Development of thick film PECVD amorphous silicon with low stress for MEMS applications
Author(s): Bangtao Chen; Francis E. H. Tay; Ciprian Iliescu
Format Member Price Non-Member Price
PDF $14.40 $18.00
cover GOOD NEWS! Your organization subscribes to the SPIE Digital Library. You may be able to download this paper for free. Check Access

Paper Abstract

This paper presents a solution for the deposition of thick amorphous silicon (α-Si:H) in plasma-enhanced chemical vapor deposition (PECVD) reactors for MEMS applications. Thick α-Si film up to 2 μm is widely used as a sacrificial layer in the MEMS release process, however, the film quality and smoothness are limited by the cracking or peeling of thick film due to their intrinsic stress. This achievement of as thick as 12 μm film was possible by tuning the deposition parameters to a 'zero' value of the residual stress in the α-Si:H layer. The influence of the PECVD process parameters, such as power, frequency mode, temperature, pressure and SiH4/Ar flow rates on tuning the residual stress and a good deposition rate was analyzed. As a result, an almost "zero-stress" α-Si:H film and a deposition rate of 85nm/min was achieved for a temperature of 200ºC, a pressure of 800 mTorr, a high-frequency power of 120W, with SiH4 flow rate of 120 sccm and Ar flow rate of 500 sccm. The deposition of low-stress and thick (more than 12 μm in our case) α-Si:H layers was possible without generation of peeling or hillock defects. Finally, the paper presents some MEMS applications of such a deposited α-Si:H layer: a very good masking layer for dry and deep wet etching of glass; and a sacrificial layer for dry or wet release of bridge/cavity structure.

Paper Details

Date Published: 30 December 2008
PDF: 11 pages
Proc. SPIE 7269, Micro- and Nanotechnology: Materials, Processes, Packaging, and Systems IV, 72690M (30 December 2008); doi: 10.1117/12.810441
Show Author Affiliations
Bangtao Chen, Institute of Bioengineering and Nanotechnology (Singapore)
Francis E. H. Tay, Institute of Bioengineering and Nanotechnology (Singapore)
Ciprian Iliescu, Institute of Bioengineering and Nanotechnology (Singapore)


Published in SPIE Proceedings Vol. 7269:
Micro- and Nanotechnology: Materials, Processes, Packaging, and Systems IV
Jung-Chih Chiao; Alex J. Hariz; David V. Thiel; Changyi Yang, Editor(s)

© SPIE. Terms of Use
Back to Top