Water splitting property of Gd1-xBixVO4 powder photocatalysts and their thin film photoelectrodes
Author(s): Hiroshi Kishida; Yuta Imagawa; Takeshi Yamaguchi; Shigeo Sato; Hironori Arakawa
Format Member Price Non-Member Price
PDF $14.40 $18.00
cover GOOD NEWS! Your organization subscribes to the SPIE Digital Library. You may be able to download this paper for free. Check Access

Paper Abstract

New water splitting solid solution photocatalysts with the composition of Gd1-xBixVO4 (x = 0, 0.3, 0.5, 0.7, 0.8, 0.9, 0.95, 1.0) were synthesized by a solid-state reaction. Gd0.3Bi0.7VO4 was found as novel photocatalyst with both O2 evolution from aqueous solution of sacrificial reagent AgNO3 under visible-light irradiation (λ > 420nm) and H2 evolution from aqueous solution of sacrificial reagent CH3OH under near visible-light irradiation (λ > 380nm). The obtained solid solutions such as GdVO4, Gd0.7Bi0.3VO4, Gd0.5Bi0.5VO4, and Gd0.3Bi0.7VO4 crystallized in zircon-tetragonal crystal structures, while Gd0.05Bi0.95VO4 and BiVO4 crystallized in scheelite-monoclinic structures. The diffuse reflectance spectra of the solid solutions shift monotonically to a long wavelength as the ratio of Bi ions to Gd ions increases in the solid solution. The structure and water splitting activity were discussed in relation to the solid solution compositions and photophysical properties. Furthermore, new thin film photoelectrodes of Gd0.7Bi0.3VO4 and BiVO4 for solar hydrogen production were prepared by metal organic decomposition (MOD) method and polymerized complex (PC) method. The photoelectrodes were characterized by using Grazing Incidence X-ray Analysis (GIXA), SEM, cyclic voltammetry (CV) and IPCE measurement. Finally, solar energy conversion efficiency for water splitting (STH efficiency) was measured. Best STH efficiencies of BiVO4 and Gd0.3Bi0.7VO4 thin film photoelectrodes were 0.05% at the applied potential of 0.9 V and 0.025% at the applied potential of 0.5 V vs NHE, respectively.

Paper Details

Date Published: 28 August 2008
PDF: 12 pages
Proc. SPIE 7044, Solar Hydrogen and Nanotechnology III, 70440B (28 August 2008); doi: 10.1117/12.794652
Show Author Affiliations
Hiroshi Kishida, Tokyo Univ. of Science (Japan)
Yuta Imagawa, Tokyo Univ. of Science (Japan)
Takeshi Yamaguchi, Tokyo Univ. of Science (Japan)
Shigeo Sato, Nissan Arc, Ltd. (Japan)
Hironori Arakawa, Tokyo Univ. of Science (Japan)


Published in SPIE Proceedings Vol. 7044:
Solar Hydrogen and Nanotechnology III
Gunnar Westin, Editor(s)

© SPIE. Terms of Use
Back to Top