Fast bender actuators for fish-like aquatic robots
Author(s): S. T. McGovern; G. M. Spinks; B. Xi; G. Alici; V. Truong; G. G. Wallace
Format Member Price Non-Member Price
PDF $14.40 $18.00

Paper Abstract

Small, highly-mobile "swimming" robots are desired for underwater monitoring operations, including pollution detection, video mapping and other tasks. Actuator materials of all types are of interest for any application where space is limited. This constraint certainly applies to the small-scale swimming robot, where multiple small actuators are needed for forward/backward propulsion, steering and diving/surfacing. A number of previous studies have demonstrated propulsion of floating objects using IPMC type polymer actuators [1-3] or piezoceramic actuators [4, 5]. Here, we show how propulsion is also possible using a multi-layer polypyrrole bimorph actuator. The actuator is based on our previously published work showing very fast resonance actuation in polypyrrole bending-type actuators [6]. The bending actuator is a tri-layer structure, in which the gold-PVDF (porous poly(vinylidene fluoride) membrane) substrate was coated on both sides with polypyrrole layers to form an electrochemical cell. Polypyrrole films on gold coated PVDF were grown galvanostatically at a current density of 0.10 mA/cm2 for 12 hours from propylene carbonate (PC) solution containing 0.1 M Li+TFSI-, 0.1 M pyrrole and 1% (w/w) water. The polypyrrole deposited PVDF was thoroughly rinsed with acetone and stored in 0.1 M Li+TFSI- / PC solution. The edges of the bulk film were trimmed off and the bending actuators were prepared as rectangular strips typically 2mm wide and 25 mm long. These actuators gave fast operation in air (to 90 Hz), and were utilised as active flexural joints on the tail fin of a fishshaped floating "boat". The actuators were attached to a simple truncated shaped fin and the deflection angle was analysed in both air and liquid for excitation with +/- 1V square wave at a range of frequencies. The mechanical resonance of the fin was seen to be 4.5 Hz in air and 0.45 Hz in PC, which gave deflection angles of approximately 60° and 55° respectively. The boat contained a battery, receiver unit and electronic circuit attached to the actuator fin assembly. Thus, the boat could be operated by remote control, and by varying the frequency and duty cycle applied to the actuator, the speed and direction of the boat could be controlled. The boat had a turning circle as small as 15 cm in radius and a maximum speed of 2m/min when operating with a tail frequency of approximately 0.7 Hz. The efficiency of the flapping tail fin was analysed and it was seen that operation at this frequency corresponded with a Strouhal number in the optimal range.

Paper Details

Date Published: 10 April 2008
PDF: 12 pages
Proc. SPIE 6927, Electroactive Polymer Actuators and Devices (EAPAD) 2008, 69271L (10 April 2008); doi: 10.1117/12.784977
Show Author Affiliations
S. T. McGovern, Univ. of Wollongong (Australia)
ARC Ctr. for Electromaterials Science (Australia)
G. M. Spinks, Univ. of Wollongong (Australia)
ARC Ctr. for Electromaterials Science (Australia)
B. Xi, Univ. of Wollongong (Australia)
ARC Ctr. for Electromaterials Science (Australia)
G. Alici, Univ. of Wollongong (Australia)
V. Truong, Defence Science and Technology Organisation (Australia)
G. G. Wallace, Univ. of Wollongong (Australia)
ARC Ctr. for Electromaterials Science (Australia)

Published in SPIE Proceedings Vol. 6927:
Electroactive Polymer Actuators and Devices (EAPAD) 2008
Yoseph Bar-Cohen, Editor(s)

© SPIE. Terms of Use
Back to Top