Low-temperature annealing of ion-doped layers of silicon in hydrogen atom flow
Author(s): V. Kagadei; E. Nefyodtsev; S. Romanenko
Format Member Price Non-Member Price
PDF $14.40 $18.00
cover GOOD NEWS! Your organization subscribes to the SPIE Digital Library. You may be able to download this paper for free. Check Access

Paper Abstract

Investigation of low-temperature annealing of Si samples implanted by As+ and Sb+ ions under influence of intensive low-energy hydrogen atom flow (j = 1015 cm-2 s-1) was carried out. It was shown, that samples, annealed in atomic hydrogen, have increased mobility and concentration of charge carriers, in comparison with samples annealed in vacuum. The phenomenon was observed in the temperature interval 300-500°C and it was investigated by Hall effect method and Reserford Backscattering Spectroscopy (RBS) of He+ ions. Positive influence of atomic hydrogen on electrical parameters of implanted layers was already revealed in the case of short process duration (5 minutes) and it was most brightly revealed at T = 300-400°C. At the same time, the influence of atomic hydrogen on annealing of self-interstitial defects in Si samples, implanted by Sb+ ions with doze 3×1014 cm-2, was insignificant. Moreover, in the case of low implantation doze (3×1013 cm-2) atomic hydrogen reduces defect annealing. Factors that may be responsible for existence of hydrogen-stimulated annealing phenomenon of implanted layers are discussed.

Paper Details

Date Published: 10 June 2006
PDF: 9 pages
Proc. SPIE 6260, Micro- and Nanoelectronics 2005, 626004 (10 June 2006); doi: 10.1117/12.676913
Show Author Affiliations
V. Kagadei, Research Institute of Semiconductor Devices (Russia)
E. Nefyodtsev, lnstitute of High Current Electronics (Russia)
S. Romanenko, lnstitute of High Current Electronics (Russia)


Published in SPIE Proceedings Vol. 6260:
Micro- and Nanoelectronics 2005
Kamil A. Valiev; Alexander A. Orlikovsky, Editor(s)

© SPIE. Terms of Use
Back to Top