Charge carrier mobility in CBP films doped with Ir(ppy)3
Author(s): Mikhail A. Parshin; Jeroen Ollevier; Mark Van der Auweraer
Format Member Price Non-Member Price
PDF $14.40 $18.00

Paper Abstract

We present the systematic study of charge carrier mobility in 4,4'-N,N'-dicarbazole-biphenyl (CBP) films doped with a triplet-emitter material tris(2-phenylpyridine) iridium (Ir(ppy)3) - 1 wt% and 10 wt%. The hole mobility was investigated with the time-of-flight (TOF) technique, as a function of electric field in the range 105 - 2 × 106 V/cm. For a CBP film doped with 1% of Ir(ppy)3 the hole mobility was also measured as a function of temperature from 20° C to 70° C. The obtained hole mobilities in CBP film doped with 1% of Ir(ppy)3 are in the range 5 × 10-10 - 3 × 10-7 cm2/Vs. The measured dependence of the hole mobility on temperature and electric field is explained in the framework of the Gaussian disorder model of Bassler. Calculated values for the effective energetic and the positional disorder are 162 meV and 4.2, respectively. The activation energy at zero field is 0.58 eV. The mobility extrapolated to zero field and infinite temperature amounts to 6 × 10-4 cm2/Vs. In CBP film doped with 10% of Ir(ppy)3 the hole mobilities are in the range 2 × 10-8 - 3 × 10-7 cm2/Vs. The observed increase of the hole mobility in Ir(ppy)3-doped CBP films with increasing doping concentration can be attributed to hopping transport of charge carries via dopant molecules.

Paper Details

Date Published: 20 April 2006
PDF: 8 pages
Proc. SPIE 6192, Organic Optoelectronics and Photonics II, 61922A (20 April 2006); doi: 10.1117/12.663553
Show Author Affiliations
Mikhail A. Parshin, Katholieke Univ. Leuven (Belgium)
Jeroen Ollevier, Katholieke Univ. Leuven (Belgium)
Mark Van der Auweraer, Katholieke Univ. Leuven (Belgium)


Published in SPIE Proceedings Vol. 6192:
Organic Optoelectronics and Photonics II
Paul L. Heremans; Michele Muccini; Eric A. Meulenkamp, Editor(s)

© SPIE. Terms of Use
Back to Top