Novel low-dielectric constant photodefinable polyimides for low-temperature polymer processing
Author(s): Kazuhiro Yamanaka; Michael Romeo; Kazuhiko Maeda; Clifford L. Henderson
Format Member Price Non-Member Price
PDF $14.40 $18.00

Paper Abstract

Current photosensitive polyimide formulations that can be developed in aqueous alkaline developers are based on the use of either (1) soluble poly(amic acid) precursor polymers or (2) polyimides functionalized with hydrophilic groups (e.g. phenol). The use of poly(amic acid) polymers requires the subsequent high temperature thermal cyclization of the polymer after imaging to produce the desired polyimide which can prevent ue of such materials in many applications. However, the use of pre-imidized poliyimides by imparting solubility with hydrophilic groups also is problematic since the presence of such groups in the polymer generally degrades the dielectric constant and water uptake performance of such materials. The goal of the work in this paper was to overcome these problems by developing new low dielectric constant polyimides that can be formulated into photo-definable materials and processed at low temperatures. In this work the use of a novel hexafluoroisopropanol (HFA)-substituted diamine to synthesize novel poly(amic-acid) and polyimide polymers is reported. The addition of HFA to the polymers is shown to produce polyimides which are soluble in both common casting solvents and 0.26 N TMAH alkaline developers. A photosentitive polyimide composition based on formulation of the HFA-subtituted polyimide with 20 wt% of a DNQ inhibitor is shown to produce high resolution patterns with a sensitivity of 170 mJ/cm2 and a contrast of 1.32 using I-line exposure. The HFA groups in the polymers are contained on a substituent group attached to the main chain by an ester linkage. It is shown that these HFA-substituent side-groups can be easily removed from the polymer after development of the patterned image by thermal treatment of the polymer at temperatures above 280 oC. The cleavage of the HFA side groups produces a polymer which does not swell and is insoluble in aqueous alkaline developers. Polyimide film properties including dissolution rate, dielectric constant, thermal expansion coefficient (CTE), water absorption have been measured and are shown to be strongly dependent on the presence of the HFA side groups. In particular, the dielectric constant of the polyimide is shown to decrease dramatically from 3.20 to 2.60 after thermal cleavage of the HFA side groups using a thermal cure at 350 oC for 30 minutes. In general, the strategy of using solubility enhancing functional groups that can be cleaved from the polymer during or after imaging and development appears to be a very promising strategy for developing photo-definable low dielectric constant polymers that can be processed at low temperatures.

Paper Details

Date Published: 29 March 2006
PDF: 11 pages
Proc. SPIE 6153, Advances in Resist Technology and Processing XXIII, 61531H (29 March 2006); doi: 10.1117/12.655600
Show Author Affiliations
Kazuhiro Yamanaka, Georgia Institute of Technology (United States)
Central Glass Co., Ltd. (Japan)
Michael Romeo, Georgia Institute of Technology (United States)
Kazuhiko Maeda, Central Glass Co., Ltd. (Japan)
Clifford L. Henderson, Georgia Institute of Technology (United States)


Published in SPIE Proceedings Vol. 6153:
Advances in Resist Technology and Processing XXIII
Qinghuang Lin, Editor(s)

© SPIE. Terms of Use
Back to Top