Magnetostriction and surface-energy-induced selective grain growth in rolled Galfenol doped with sulfur
Format Member Price Non-Member Price
PDF $14.40 $18.00
cover GOOD NEWS! Your organization subscribes to the SPIE Digital Library. You may be able to download this paper for free. Check Access

Paper Abstract

The surface-energy-induced selective grain growth with a specific surface plane can be governed in polycrystalline (Fe81.3Ga18.7) + 0.5at.%B alloys doped with sulfur by controlling the segregation of sulfur through conventional rolling and texture annealing, where boron improves ductility due to suppressing grain boundary fracture during rolling process. The textured sheet, which was annealed at 1200°C for 2h under flowing argon and then quenched in water, exhibits a maximum magnetostriction of about 200 ppm along the rolling direction. During an argon annealing process, a convex profile in magnetostriction as a function of annealing time is formed. As the annealing temperature increases, the observed peak in the convex profiles shifts to less annealing time and also narrows. As-rolled (Fe81.3Ga18.7) + 0.5 at.%B + 0.005 at.%S sheets with large amounts of sub-grain which most likely have been deformed by the rolling process have some {100} and {111} grains parallel to the rolling direction. While texture annealing appears to eliminate the majority of the sub-grains present to below 1% of sub-structured or deformed area in the sheet annealed at 1200°C for 2h. From a texture standpoint the some clustered {100} poles were found and ~25° away from the rolling direction. And the {100} poles are centered right on the rolling direction for the highly textured subset.

Paper Details

Date Published: 16 May 2005
PDF: 8 pages
Proc. SPIE 5761, Smart Structures and Materials 2005: Active Materials: Behavior and Mechanics, (16 May 2005); doi: 10.1117/12.599743
Show Author Affiliations
Suok-Min Na, Univ. of Maryland/College Park (United States)
Alison B. Flatau, Univ. of Maryland/College Park (United States)


Published in SPIE Proceedings Vol. 5761:
Smart Structures and Materials 2005: Active Materials: Behavior and Mechanics
William D. Armstrong, Editor(s)

© SPIE. Terms of Use
Back to Top