Research on surface modification of nano-zirconia
Author(s): Wen Chen; Cun-Lin Zhang; Xiao-Yi Yang
Format Member Price Non-Member Price
PDF $17.00 $21.00

Paper Abstract

The mechanisms about the aggregation and dispersibility of nano-zirconia were analyzed in detail. And nano-zirconia powders which were surface-modified with silane coupling reagent WD70 were prepared in order to disperse homogeneously in ethanol in this investigation. The grain size and grain phase of nano-zirconia were obtained by XRD. Research and characterization on the structure and surface characteristic of surface-modified nano-zirconia were achieved by XPS, TG-DSC, TEM and FT-IR. The results given by FT-IR and XPS showed WD70 was jointed on the surface of nano-zirconia through both physical adsorption and chemical binding after the de-methanol reaction between the methoxyl groups of WD70 and the hydroxy groups on the surface of nano-zirconia. And the corresponding model of surface-modified nano-zirconia was given. The images provided by TEM presented intuitionistic effect of surface modification on the dispersibility of nano-zirconia in ethanol. And TG-DSC analysis ascertained the amount of WD70 that was jointed on the surface of nano-zirconia and the amount was about 6.21 percent.

Paper Details

Date Published: 9 February 2005
PDF: 9 pages
Proc. SPIE 5635, Nanophotonics, Nanostructure, and Nanometrology, (9 February 2005); doi: 10.1117/12.577969
Show Author Affiliations
Wen Chen, Capital Normal Univ. (China)
Cun-Lin Zhang, Capital Normal Univ. (China)
Xiao-Yi Yang, Capital Normal Univ. (China)


Published in SPIE Proceedings Vol. 5635:
Nanophotonics, Nanostructure, and Nanometrology
Xing Zhu; Stephen Y. Chou; Yasuhiko Arakawa, Editor(s)

© SPIE. Terms of Use
Back to Top