Investigation of the growth and the holographic storage properties of Fe:LiTaO3 crystal
Author(s): Caixia Liu; Tao Zhang; Shouzhi Zhao
Format Member Price Non-Member Price
PDF $14.40 $18.00

Paper Abstract

The LiTaO3 crystal doped with 0.03 wt% Fe2O3 was grown in a diameter-controlled Czochraski equipment using Si-Mo bar heater furnace. The photo-damage resistance ability, exponential gain coefficient, diffraction efficiency and response time of Fe:LiTaO3 and Fe:LiNbO3 crystals were measured. The measured results showed that the photo-damage resistance ability of Fe:LiTaO3 crystal was as much as 5 times higher than that of Fe:LiNbO3, the response speed of Fe:LiTaO3 crystal was improved one order of magnitude than that of Fe:LiNbO3, and the exponential gain coefficient and diffraction efficient of Fe:LiTaO3 crystal were smaller than that of Fe:LiNbO3, respectively. Using Fe:LiTaO3 crystal as recording medium, the obtained image was clear and complete in the holographic associative memory experiment using self-pump phase conjugate reflector.

Paper Details

Date Published: 3 January 2005
PDF: 5 pages
Proc. SPIE 5643, Advances in Optical Data Storage Technology, (3 January 2005); doi: 10.1117/12.574258
Show Author Affiliations
Caixia Liu, Harbin Institute of Technology (China)
Tao Zhang, Harbin Institute of Technology (China)
Shouzhi Zhao, Harbin Institute of Technology (China)


Published in SPIE Proceedings Vol. 5643:
Advances in Optical Data Storage Technology
Duanyi Xu; Kees A. Schouhamer Immink; Keiji Shono, Editor(s)

© SPIE. Terms of Use
Back to Top