Improvement of ohmic contact to P-type GaN using two-step activation processing
Author(s): Zhi-Nong Yu; Wei Xue; Jong-Wook Seo; Soon-Jae Yu
Format Member Price Non-Member Price
PDF $14.40 $18.00
cover GOOD NEWS! Your organization subscribes to the SPIE Digital Library. You may be able to download this paper for free. Check Access

Paper Abstract

A two-step rapid thermal annealing (RTA) process was investigated for electrical activation of magnesium doped GaN layer. The samples were studied by room temperature Hall measurements and I-V curve. In the two-step RTA process, the first low temperature step (600°C) with a long annealing time (4 min) was followed by the second high temperature (850°C) step with a short annealing time. A hole concentration of 1.39×1018cm-3 was achieved for the activated sample. And the specific contact resistance for Ni/Au-contacted p-GaN was determined to be 1.8×10-4Ω.cm2, These results show that the two-step RTA process significantly improves the electrical properties of P-GaN layer compared to the one-step RTA process.

Paper Details

Date Published: 31 January 2005
PDF: 4 pages
Proc. SPIE 5624, Semiconductor and Organic Optoelectronic Materials and Devices, (31 January 2005); doi: 10.1117/12.572520
Show Author Affiliations
Zhi-Nong Yu, Beijing Institute of Technology (China)
Wei Xue, Beijing Institute of Technology (China)
Jong-Wook Seo, Hongik Univ. (South Korea)
Soon-Jae Yu, Itswell Co., Ltd. (South Korea)


Published in SPIE Proceedings Vol. 5624:
Semiconductor and Organic Optoelectronic Materials and Devices
Chung-En Zah; Yi Luo; Shinji Tsuji, Editor(s)

© SPIE. Terms of Use
Back to Top