Nondestructive mechanical imaging of SnO2 nanobelts
Author(s): Yuegui Zheng; Robert E. Geer
Format Member Price Non-Member Price
PDF $14.40 $18.00

Paper Abstract

The relative surface contact stiffness of SnO2 nanobelts has been investigated via nondestructive ultrasonic force microscopy (UFM). The nanobelt crystal structure, as determined via transmission electron microscopy, was indexed to the tetragonal rutile structure (with lattice constants identical to those of bulk SnO2) as reported previously. The atomic Sn:O composition of the nanobelts studied was at or near 1:2. Topographic imaging studies revealed the nanobelt surface to be atomically flat with the exception of surface nano-dots, assumed to be local SnO2 crystallites. Preliminary local (10nm x 10nm) reduced modulus measurements were carried out via differential UFM on both the flat and nanodot regions of the nanobelt. Using the underlying Si substrate as a calibration standard the SnO2 modulus was estimated at 157±12 GPa, significantly lower than corresponding bulk values for any of the observed crystal orientations. We speculate this discrepancy is due in part to a combination of the aspherical probe tip and unknown adhesive properties of nanobelt, although an intrinsic reduction of the SnO2 nanobelt modulus cannot be ruled out.

Paper Details

Date Published: 21 July 2004
PDF: 7 pages
Proc. SPIE 5392, Testing, Reliability, and Application of Micro- and Nano-Material Systems II, (21 July 2004); doi: 10.1117/12.540411
Show Author Affiliations
Yuegui Zheng, Univ. at Albany (United States)
Robert E. Geer, Univ. at Albany (United States)


Published in SPIE Proceedings Vol. 5392:
Testing, Reliability, and Application of Micro- and Nano-Material Systems II
Norbert Meyendorf; George Y. Baaklini; Bernd Michel, Editor(s)

© SPIE. Terms of Use
Back to Top