Adhesion strength measurements of excimer-laser-treated PTFE surfaces using liquid photoreagents
Author(s): Bela Hopp; Tomi Smausz; Norbert Kresz; Ferenc Ignacz
Format Member Price Non-Member Price
PDF $14.40 $18.00

Paper Abstract

The most known feature of polytetrafluoroethylene (PTFE) is its adhesion behavior: it is hydrophobic and oleophobic at the same time. This can cause serious problems and obstacles during the surface treatment and fixing of PTFE objects. During our experiments Teflon films were irradiated by an ArF excimer laser beam in presence of liquid photoreagents containing amine groups (aminoethanol, 1,2-diaminoethane, triethylene-tetramine). In consequence of the treatment the adhesion of the modified surfaces significantly increased, the samples could be glued and moistened. The adhesion strength of the glued surfaces was measured in the function of the applied laser fluence. The adhesion strength increased drastically between 0 - 1 mJ/cm2 and showed saturation above 1 mJ/cm2 at approximately 5 - 9 MPa values depending on the applied photoreagents. On the basis of our experiments it was found that the treatment with triethylene-tetramine was the most effective. The surface chemical modifications of the treated Teflon samples can be due to the incorporation of amine groups into the surface layer.

Paper Details

Date Published: 9 April 2003
PDF: 5 pages
Proc. SPIE 5131, Third GR-I International Conference on New Laser Technologies and Applications, (9 April 2003); doi: 10.1117/12.513608
Show Author Affiliations
Bela Hopp, Univ. of Szeged (Hungary)
Tomi Smausz, Univ. of Szeged (Hungary)
Norbert Kresz, Univ. of Szeged (Hungary)
Ferenc Ignacz, Univ. of Szeged (Hungary)


Published in SPIE Proceedings Vol. 5131:
Third GR-I International Conference on New Laser Technologies and Applications
Alexis Carabelas; Giuseppe Baldacchini; Paolo Di Lazzaro; Dimitrios Zevgolis, Editor(s)

© SPIE. Terms of Use
Back to Top