Study on no fanning noise holographic storage of tri-doped Mg:In:Fe:LiNbO3 crystals
Author(s): Jun Wang; Zhonghua Zhang; Rui Wang
Format Member Price Non-Member Price
PDF $14.40 $18.00
cover GOOD NEWS! Your organization subscribes to the SPIE Digital Library. You may be able to download this paper for free. Check Access

Paper Abstract

Doped MgO and In2O3 in Fe:LiNbO3 through Czochralski technology to grow Mg:In:Fe:LiNbO3 crystal for the first time. The photo-scattering resistance ability of Mg(3mol%):In(3mol%):Fe:LiNbO3 crystal were measured. It improves the two orders magnitude higher than that of Fe:LiNbO3 crystal. The absorption spectra of the Mg:In:Fe:LiNbO3 crystals were tested. The absorptive edge was found to shift to the short wavelength. The infrared spectra of the crystals were measured, when Mg2+ and In3+ reach their threshold concentration in crystal, the absorption peak shifts from 3484cm-1 to 3520cm-1. Two wave coupling method was used to test the diffraction efficiency and response time of the crystals. The response speed of the Mg:In:Fe:LiNbO3 crystal is higher than that of the Fe:LiNbO3 crystal.

Paper Details

Date Published: 9 April 2003
PDF: 4 pages
Proc. SPIE 5060, Sixth International Symposium on Optical Storage (ISOS 2002), (9 April 2003); doi: 10.1117/12.510398
Show Author Affiliations
Jun Wang, Harbin Institute of Technology (China)
Zhonghua Zhang, Harbin Institute of Technology (China)
Rui Wang, Harbin Institute of Technology (China)


Published in SPIE Proceedings Vol. 5060:
Sixth International Symposium on Optical Storage (ISOS 2002)
Fuxi Gan; Zuoyi Li, Editor(s)

© SPIE. Terms of Use
Back to Top