Corrosion-resistant nickel superalloy coatings laser clad with a 6-kW high-power diode laser (HPDL)
Author(s): Jari Tuominen; Mari Honkanen; Jari Hovikorpi; Jorma Vihinen; Petri Vuoristo; Tapio Maentylae
Format Member Price Non-Member Price
PDF $14.40 $18.00
cover GOOD NEWS! Your organization subscribes to the SPIE Digital Library. You may be able to download this paper for free. Check Access

Paper Abstract

A series of exerpiments were performed to investigate the one-step laser cladding of Inconel 625 powder, injected off-axially onto Fe37 and 42CrMo4 substrates. The experiments were carried out using a 6 kW high power diode laser (HPDL) mounted to a 6 axis robot system. The rectangular shape of the delivering beam was focused to a spot size of 22 x 5 mm on the work piece. The coating samples were produced using different levels of powder feed rate (77 - 113 g/min), traveling speed (300 - 400 mm/min) and laser power (4.8 - 6 kW). Hot corrosion resistance of laser-clad Inconel 625 coatings were tested in Na2SO4 - V2O5 at 650°C for 1000 hours. Wet corrosion properties of the obtained coatings were tested in immersion tests in 3.5 wt.% NaCl solution. Diode laser power of 6 kW (808 and 940 nm) was high enough to produce 20 mm wide laser-clad tracks with a thickness of 2.5 mm in a single pass, when powder feed rate was more than 6 kg/h and traverse speed was 400 mm/min. Wet corrosion properties of laser-clad Inconel 625 coatings were found to be superior to sprayed and welded coatings. Hot corrosion resistance was even slightly better than corresponding wrought alloy. Finally, one-step HPDL cladding was demonstrated in coating of shaft for hydraulic cylinder with Inconel 625 powder. Due to high coating quality, high deposition rate and traverse speed HPDL devices are very promising for large area cladding applications.

Paper Details

Date Published: 3 March 2003
PDF: 6 pages
Proc. SPIE 4831, First International Symposium on High-Power Laser Macroprocessing, (3 March 2003); doi: 10.1117/12.497958
Show Author Affiliations
Jari Tuominen, Tampere Univ. of Technology (Finland)
Mari Honkanen, Tampere Univ. of Technology (Finland)
Jari Hovikorpi, Tampere Univ. of Technology (Finland)
Jorma Vihinen, Tampere Univ. of Technology (Finland)
Petri Vuoristo, Tampere Univ. of Technology (Finland)
Tapio Maentylae, Tampere Univ. of Technology (Finland)


Published in SPIE Proceedings Vol. 4831:
First International Symposium on High-Power Laser Macroprocessing
Isamu Miyamoto; Kojiro F. Kobayashi; Koji Sugioka; Reinhart Poprawe; Henry Helvajian, Editor(s)