Equilibrium sorption and rate of diffusion of water into photoresist thin films
Format Member Price Non-Member Price
PDF $14.40 $18.00
cover GOOD NEWS! Your organization subscribes to the SPIE Digital Library. You may be able to download this paper for free. Check Access

Paper Abstract

The equilibrium resist film water content at various water partial pressures and the rate of diffusion of water into photoresist thin films was investigated fro three model resist polymers: (1) a traditional novolac matrix, (2) poly(p-hydroxystyrene), and (3) bis-trifluoromethyl carbinol substituted polynorbornene. A quartz crystal microbalance (QCM) was used to measure the mass of water added to resist films exposed to environments of differing relative humidity. All three polymer systems absorbed significant quantities of water at 100% relative humidity with PHOST absorbing the most (9.8wt.%) followed by the polynorbornenes (5-8 wt%) and the novolacs (2-3 wt%). The diffusion of water into the polymer films was observed to follow Fickian diffusion behavior initially (Mt/Ms<0.6) followed by behavior indicative of concentration dependent diffusion at large water uptake values. Finally, interdigitated electrodes were utilized to estimate the impact of varying humidity upon the net dielectric constant of the resist films. A linear relationship was observed for measured capacitance versus water uptake for all polymers measured and a power law dielectric mixing rule was found to properly describe the effective dielectric constant of the water/polymer mixtures.

Paper Details

Date Published: 12 June 2003
PDF: 12 pages
Proc. SPIE 5039, Advances in Resist Technology and Processing XX, (12 June 2003); doi: 10.1117/12.485079
Show Author Affiliations
Cody M. Berger, Georgia Institute of Technology (United States)
Clifford L. Henderson, Georgia Institute of Technology (United States)


Published in SPIE Proceedings Vol. 5039:
Advances in Resist Technology and Processing XX
Theodore H. Fedynyshyn, Editor(s)