Effect of composition on the magnetic and elastic properties shape-memory Ni-Mn-Ga
Author(s): Aayush Malla; Marcelo J. Dapino; Thomas A. Lograsso; Deborah Schlagel
Format Member Price Non-Member Price
PDF $14.40 $18.00
cover GOOD NEWS! Your organization subscribes to the SPIE Digital Library. You may be able to download this paper for free. Check Access

Paper Abstract

The growing interest in ferromagnetic shape-memory Ni-Mn-Ga for implementation in actuator applications originates from the fact that this class of materials exhibits large strains when driven by a magnetic field. Large bidirectional strains up to a theoretical 6% are produced in these materials by twin boundary motion as martensite variants rotate to align respectively parallel or perpendicular to applied magnetic fields or stresses. These strains represent a significant improvement over piezoelectric and magnetostrictive materials. In this paper, we report on experimental measurements conducted on Ni-Mn-Ga cylindrical rods subjected to uniaxial stresses and uniaxial magnetic fields which were applied collinearly along the magnetic easy axis direction of the rods. To this end, a test apparatus was developed which consists of a water-cooled solenoid actuator and a loading fixture. Despite the lack of a readily recognizable mechanism for reversible deformations, bidirectional strains as large as 4300 ppm (0.43%) were observed, or three times the saturation magnetostriction of Terfenol-D. This paper presents room-temperature data including magnetization hysteresis, strain versus field and peak strain versus stress curves collected over a range of stresses between 0-65 MPa. From the latter set of curves, blocking force values are estimated as those for which the strain is 1% of the maximum (zero-load) strain. The results illustrate the sensitivity of material behavior with respect to composition at different driving conditions and offer insight on the choice of material compositions at which maximum actuation performance is achieved.

Paper Details

Date Published: 13 August 2003
PDF: 12 pages
Proc. SPIE 5053, Smart Structures and Materials 2003: Active Materials: Behavior and Mechanics, (13 August 2003); doi: 10.1117/12.484359
Show Author Affiliations
Aayush Malla, Ohio State Univ. (United States)
Marcelo J. Dapino, Ohio State Univ. (United States)
Thomas A. Lograsso, Iowa State Univ. (United States)
Deborah Schlagel, Iowa State Univ. (United States)


Published in SPIE Proceedings Vol. 5053:
Smart Structures and Materials 2003: Active Materials: Behavior and Mechanics
Dimitris C. Lagoudas, Editor(s)