Laser cladding Ni35A120Fe intermetallic coating for resisting high-temperature oxidation and hot corrosion
Author(s): Xiangyang Xu; Minlin Zhong; Wenjin Liu
Format Member Price Non-Member Price
PDF $14.40 $18.00
cover GOOD NEWS! Your organization subscribes to the SPIE Digital Library. You may be able to download this paper for free. Check Access

Paper Abstract

With Ni/Al cladding powders and coaxial powder-feeding mode, Ni35A12OFe intermetallic coating was successfully prepared by laser cladding. The optimizing principles of processing parameters of laser cladding were proposed. The shaping and microstructure of laser cladding coating were analyzed. The experimental results indicated that lower laser power; slower scanning velocity and larger beam diameter could ensure excellent shaping and metallurgical quality. Under the optimum processing, laser cladding Ni35Al2OFe intermetallic coating was free of porosity and cracks and a fully metallurgical adhesion was achieved between the coating and the substrate. The microstructure was composed of refine ?-NiAl intermetallic phase as the base and a few dispersed ? phase particles precipitated along crystal grain boundaries and within the grains. The formation of ?-NiAl phase dissolved with Fe, precipitation of ductile ? phase and refined crystal grains were favorable of not only higher strength but also enough ductility and toughness of laser cladding coating.

Paper Details

Date Published: 12 September 2002
PDF: 7 pages
Proc. SPIE 4915, Lasers in Material Processing and Manufacturing, (12 September 2002); doi: 10.1117/12.482891
Show Author Affiliations
Xiangyang Xu, Tsinghua Univ. (China)
Minlin Zhong, Tsinghua Univ. (China)
Wenjin Liu, Tsinghua Univ. (China)


Published in SPIE Proceedings Vol. 4915:
Lasers in Material Processing and Manufacturing
ShuShen Deng; Tatsuo Okada; Klaus Behler; XingZong Wang, Editor(s)

© SPIE. Terms of Use
Back to Top