Evolution of optical properties of tris (8-hydroxyquinoline) aluminum (alq3) with atmosphere exposure
Author(s): Aleksandra B. Djurisic; Tsz Wai Lau; Chung Yin Kwong; Lillian Sze Man Lam; Wai Kin Kin Chan
Format Member Price Non-Member Price
PDF $17.00 $21.00
cover GOOD NEWS! Your organization subscribes to the SPIE Digital Library. You may be able to download this paper for free. Check Access

Paper Abstract

Tris (8-hydroxyquinoline) aluminum (Alq3) represents a material of significant interest for electron transport and/or light emitting layer applications in organic light emitting diodes (OLEDs). In spite of advances in Alq3 based devices, the knowledge and understanding of the optical properties of Alq3 and its chemical and environmental stability is still limited. With the reports of decreased turn-on voltage and increased efficiency of OLEDs, the issues of lifetime and stability of those devices are attracting increasing attention. The degradation of Alq3 based OLEDs and dark spots formation and growth have been intensively studied. The studies on degradation of optical properties of Alq3 itself remain scarce. We have investigated effects of atmosphere exposure to properties of tris (8-hydroxyquinoline) aluminum (Alq3) thin films by photoluminescence (PL) and absorption measurements. Alq3 films were evaportated on glass substrates at different temperatures. The influence of annealing to the environmental stability of the films has also been investigated. It has been found that deposition at higher substrate temperature and annealing of the samples deposited at room temperature yields improvement in environmental stability of the films, i.e. less decrease of the PL intensity over time with atmosphere exposure, as well as increased PL intensity. To investigate further effects of the air exposure, films deposited at room temprature were stored for four days in air, nitrogen, and oxygen. No decrease in PL intensity has been found for storage in nitrogen, while decrease for the film stored in oxygen was smaller than that for film stored in air, indicating that both humidity and oxygen play a role in PL intensity decrease in Alq3 thin films.

Paper Details

Date Published: 3 March 2003
PDF: 8 pages
Proc. SPIE 4800, Organic Light-Emitting Materials and Devices VI, (3 March 2003); doi: 10.1117/12.451846
Show Author Affiliations
Aleksandra B. Djurisic, Univ. of Hong Kong (Hong Kong)
Tsz Wai Lau, Univ. of Hong Kong (Hong Kong)
Chung Yin Kwong, Univ. of Hong Kong (Hong Kong)
Lillian Sze Man Lam, Univ. of Hong Kong (Hong Kong)
Wai Kin Kin Chan, Univ. of Hong Kong (Hong Kong)

Published in SPIE Proceedings Vol. 4800:
Organic Light-Emitting Materials and Devices VI
Zakya H. Kafafi; Homer Antoniadis, Editor(s)

© SPIE. Terms of Use
Back to Top