Investigation of near-room-temperature self-annealing of electrochemical-deposited (ECD) blanket copper films
Author(s): Weng Hong Teh; Leong Tee Koh; Shou Mian Chen; Joseph Xie; Chao Yong Li; Pang Dow Foo
Format Member Price Non-Member Price
PDF $14.40 $18.00

Paper Abstract

Self-annealing of ECD blanket copper films on an IMP Cu (200nm)/IMP TaN PECVD SIO2 (500nm)/Si multi-layer structure with varying ECD CU thickness from 0.5micrometers to 3 micrometers is described and investigated. Sheet resistance, stress and surface topography evolution as a function of time have been monitored to provide a better understanding to the grain growth and surface agglomeration aspects of the self-annealing process. Resistivity changes, which exhibit a sigmoidal curve, are closely related with the grain size growth, which occurs during the recrystallization. However, this microstructural evolution should not be correlated to the stress relaxation effect because the films of the difference in time dependence. The self-annealing process of ECD Cu films lasts from a few hours to days and weeks depending on the plated thickness of the Cu film. The initiation of self-annealing is accompanied by an abrupt rise in the standard deviation of the sheet resistance, reflecting the possibility of abnormal grain growth during the process. Changes in the time dependence of this decrease with film thickness can be understood in view of the physical constraint of a 2D grain growth at the film boundary for thinner films. The coalescence mechanism of small grains until a full recrystallization of the layer into large twinned grains, which is used to explain the sheet resistance drop is supported by an increase in surface roughness of the ECD Cu film characterized by AFM. Diffusion or desorption of contaminant/additives in the relatively dirty process of ECD into the copper films could be a mechanism for the unusual stress release. It is found that the increase in the rate of stress relaxation scales with the thickness of the ECD Cu film. A change of the dominant factor for stress release from curvature dependent to film thickness dependent is speculated for this behavior.

Paper Details

Date Published: 24 October 2000
PDF: 8 pages
Proc. SPIE 4227, Advanced Microelectronic Processing Techniques, (24 October 2000); doi: 10.1117/12.405382
Show Author Affiliations
Weng Hong Teh, Singapore-MIT Alliance (United Kingdom)
Leong Tee Koh, Institute of Microelectronics (Singapore)
Shou Mian Chen, Institute of Microelectronics (Singapore)
Joseph Xie, Institute of Microelectronics (Singapore)
Chao Yong Li, Institute of Microelectronics (Singapore)
Pang Dow Foo, Institute of Microelectronics (Singapore)


Published in SPIE Proceedings Vol. 4227:
Advanced Microelectronic Processing Techniques
H. Barry Harrison; Andrew Thye Shen Wee; Subhash Gupta, Editor(s)

© SPIE. Terms of Use
Back to Top