Film characterization and evaluation of process performance for the modified electron beam resist
Author(s): Fu-Hsiang Ko; Jyh-Hua Ting; Cheng-Tung Chou; Li-Tung Hsiao; Tiao-Yuan Huang; Bau-Tong Dai
Format Member Price Non-Member Price
PDF $14.40 $18.00

Paper Abstract

The modification of the electron beam resist by spiking with various amounts of poly(styrene-co-maleic anhydride) copolymer is performed. The characterization of resist solutions by gel permeation chromatography (GPC) and viscosity measurement reveals the main polymer chain in the resist is unchangeable, irrespective of the amount of modification. In addition, the spiking copolymer exists in original form. The viscosity of the resist increases with the amount of spiking polymer. Our thermal analysis results show that the resist are mainly decomposed in two regions (280 and 544 degrees Celsius). The mass loss at 280 degrees Celsius is significant higher than at 544 degrees Celsius. The spectra of Fourier transform infrared red (FTIR) spectrometer indicate the extent of carbonate group decomposition decreases with temperature for resists. The plasma etching experiment indicates the promotion of etching resistance of the resist film is due to modification, while the resolution, sensitivity and contrast are not degraded. Owing to the polymer aggregation effect, the stripping performance of the resist film can achieve better after copolymer modification.

Paper Details

Date Published: 23 June 2000
PDF: 10 pages
Proc. SPIE 3999, Advances in Resist Technology and Processing XVII, (23 June 2000); doi: 10.1117/12.388268
Show Author Affiliations
Fu-Hsiang Ko, National Chiao Tung Univ. (Taiwan)
Jyh-Hua Ting, National Chiao Tung Univ. (Taiwan)
Cheng-Tung Chou, National Central Univ. (Taiwan)
Li-Tung Hsiao, National Central Univ. (Taiwan)
Tiao-Yuan Huang, National Chiao Tung Univ. (Taiwan)
Bau-Tong Dai, National Chiao Tung Univ. (Taiwan)


Published in SPIE Proceedings Vol. 3999:
Advances in Resist Technology and Processing XVII
Francis M. Houlihan, Editor(s)

© SPIE. Terms of Use
Back to Top