Optical thin films grown by surface chemical reaction for high-power lasers
Author(s): Shin-ichi Zaitsu; Shinji Motokoshi; Takahisa Jitsuno; Masahiro Nakatsuka; Tatsuhiko Yamanaka
Format Member Price Non-Member Price
PDF $17.00 $21.00

Paper Abstract

We prepared optical thin films grown with surface chemical reactions using TiCl4 and H2O for TiO2. The nonuniformity of thickness distribution was under 1% over 240 mm in diameter. The structure of TiO2 film grown at 25 degrees Celsius was amorphous. The structure changed into polycrystalline with an increase of growth temperature up to 400 degrees Celsius. Secondary ion mass spectrometry showed that chloride residents presented in the films at every growth temperature. However, these chloride residents could be removed by thermal annealing at 400 degrees Celsius. The TiO2 film at the growth temperature of 25 degrees Celsius had a laser-induced damage threshold of 5 J/cm2 for 1-ns, 1064 nm laser pulse. The damage threshold of TiO2 films decreased at higher growth temperature. Chloride in the films had no influence on the laser-induced damage threshold.

Paper Details

Date Published: 3 April 2000
PDF: 7 pages
Proc. SPIE 3889, Advanced High-Power Lasers, (3 April 2000); doi: 10.1117/12.380929
Show Author Affiliations
Shin-ichi Zaitsu, Osaka Univ. (Japan)
Shinji Motokoshi, Institute for Laser Technology (Japan)
Takahisa Jitsuno, Osaka Univ. (Japan)
Masahiro Nakatsuka, Osaka Univ. (Japan)
Tatsuhiko Yamanaka, Osaka Univ. (Japan)


Published in SPIE Proceedings Vol. 3889:
Advanced High-Power Lasers
Marek Osinski; Howard T. Powell; Koichi Toyoda, Editor(s)

© SPIE. Terms of Use
Back to Top