Crystal growth and morphology investigation with 3D luminance of photonic organic DAST thin film
Author(s): Tien-Jey Sheu; ChenYang Yui Whei; Song-Shiang Lin; Fu-Yuan Tsai; Yuan-Kuang Tu
Format Member Price Non-Member Price
PDF $14.40 $18.00
cover GOOD NEWS! Your organization subscribes to the SPIE Digital Library. You may be able to download this paper for free. Check Access

Paper Abstract

A nearly perfect single crystal DAST thin film has been grown in this study. The polarized optic microscopy photograph demonstrated an ordered morphology for the surface of this thin film. The FTIR spectrum shoed that the intensities of the characteristic absorption bands for the single crystal thin film were different from that for the crystalline thin film. With 3D luminance image analysis, it was found that the intensity of a guided laser light passing through the single crystal thin film along its a-axis is a little bit stronger than that guided along a standard 8.5/125 μm silica optic fiber. The diameter of the guided light and the space between the two guided lights estimated were about 25 μm and 65 μm, respectively. This study indicates that only the single crystal thin film can be used as a waveguide without further process and is a promising candidate for electro-optic modulators and other active optical devices.

Paper Details

Date Published: 12 November 1999
PDF: 8 pages
Proc. SPIE 3896, Design, Fabrication, and Characterization of Photonic Devices, (12 November 1999); doi: 10.1117/12.370387
Show Author Affiliations
Tien-Jey Sheu, Chung Yuan Christian Univ. (Taiwan)
ChenYang Yui Whei, Chung Yuan Christian Univ. (Taiwan)
Song-Shiang Lin, Chung Yuan Christian Univ. (Taiwan)
Fu-Yuan Tsai, Chunghwa Telecom Co., Ltd. (Taiwan)
Yuan-Kuang Tu, Chunghwa Telecom Co., Ltd. (Taiwan)


Published in SPIE Proceedings Vol. 3896:
Design, Fabrication, and Characterization of Photonic Devices
Marek Osinski; Soo-Jin Chua; Shigefusa F. Chichibu, Editor(s)

© SPIE. Terms of Use
Back to Top