Amorphous structure and properties in laser-clad Ni-Cr-Al coating on Al-Si alloy
Author(s): Gongying Liang; T. T. Wong; J. Y. Su; C. H. Woo
Format Member Price Non-Member Price
PDF $14.40 $18.00
cover GOOD NEWS! Your organization subscribes to the SPIE Digital Library. You may be able to download this paper for free. Check Access

Paper Abstract

A Ni-Cr-Al coating was clad by a 5 kW CO2 laser with different laser power on Al-Si alloy. Using transmission electron microscopy, a mixing microstructure containing Ni- based amorphous structures was observed in the laser clad zones. As the uniformity of chemical composition and temperature is poor in the laser cladding, the amorphous structure with some Ni3Al crystals coexisted in the cladding. According to the morphologies of Ni-based amorphous structures, the amorphous structure existed not only in the net-like boundaries surrounding the granular structure but also in the granular structure. The microhardness of the mixture amorphous structure is between HV 600 - 800, which is lower than that of crystal phases in the coating. A differential thermal analysis showed that Ni- based amorphous structure exhibits a higher initial crystallizing temperature (about 588 degree(s)C), which is slightly higher than that of the eutectic temperature of Al- Si alloy. The wear experimental results showed that some amorphous structure exist in the laser cladding can reduce the peeling of the granular phases from matrix, and improve the its wear resistance.

Paper Details

Date Published: 8 September 1999
PDF: 5 pages
Proc. SPIE 3862, 1999 International Conference on Industrial Lasers, (8 September 1999); doi: 10.1117/12.361092
Show Author Affiliations
Gongying Liang, Xian Jiaotong Univ. (China)
T. T. Wong, Hong Kong Polytechnic Univ. (China)
J. Y. Su, Xian Jiaotong Univ. (China)
C. H. Woo, Hong Kong Polytechnic Univ. (China)


Published in SPIE Proceedings Vol. 3862:
1999 International Conference on Industrial Lasers
Fuxi Gan; Horst Weber; Zaiguang Li; Qingming Chen, Editor(s)

© SPIE. Terms of Use
Back to Top