InGaN-based UV/blue/green/amber LEDs
Author(s): Takashi Mukai; Motokazu Yamada; Shuji Nakamura
Format Member Price Non-Member Price
PDF $14.40 $18.00
cover GOOD NEWS! Your organization subscribes to the SPIE Digital Library. You may be able to download this paper for free. Check Access

Paper Abstract

High-efficient light emitting diodes (LEDs) emitting red, amber, green, blue, and ultraviolet light have been obtained through the use of an InGaN active layers instead of GaN active layers. Red LEDs with an emission wavelength of 680 nm which emission energy was smaller than the band-gap energy of InN were fabricated mainly resulting from the piezoelectric field due to the strain. The localized energy states caused by In composition fluctuation in the InGaN active layer seem to be related to the high efficiency of the InGaN-based emitting devices in spite of having a large number of threading dislocations. InGaN single-quantum-well- structure blue LEDs were grown on epitaxially laterally overgrown GaN and sapphire substrates. The emission spectra showed the similar blue shift with increasing forward currents between both LEDs. The output power of both LEDs was almost the same, as high as 6 mW at a current of 20 mA. These results indicate that the In composition fluctuation is not caused by dislocations, the dislocations are not effective to reduce the efficiency of the emission, and that the dislocations from the leakage current pathway in InGaN.

Paper Details

Date Published: 14 April 1999
PDF: 12 pages
Proc. SPIE 3621, Light-Emitting Diodes: Research, Manufacturing, and Applications III, (14 April 1999); doi: 10.1117/12.344464
Show Author Affiliations
Takashi Mukai, Nichia Chemical Industries, Ltd. (Japan)
Motokazu Yamada, Nichia Chemical Industries, Ltd. (Japan)
Shuji Nakamura, Nichia Chemical Industries, Ltd. (United States)


Published in SPIE Proceedings Vol. 3621:
Light-Emitting Diodes: Research, Manufacturing, and Applications III
E. Fred Schubert; Ian T. Ferguson; H. Walter Yao, Editor(s)

© SPIE. Terms of Use
Back to Top