Primary radiation defect formation in silver halides
Author(s): Donats K. Millers; Larisa Grigorjeva
Format Member Price Non-Member Price
PDF $14.40 $18.00
cover GOOD NEWS! Your organization subscribes to the SPIE Digital Library. You may be able to download this paper for free. Check Access

Paper Abstract

Under irradiation the formation of primary intrinsic defects in silver halide solid solutions AgBr1-xClx take place via strong exciton-phonon interaction. Efficiency of these defects formation depend on solid solution composition and within 0 <EQ x <EQ 0.15 dependence on temperature was observed too. Estimation shows efficiency of defects creation is approximately 0.01 for AgCl and noticeably higher for AgBr.

Paper Details

Date Published: 1 January 1998
PDF: 6 pages
Proc. SPIE 3347, Optical Information Science and Technology (OIST97): Optical Recording Mechanisms and Media, (1 January 1998); doi: 10.1117/12.301440
Show Author Affiliations
Donats K. Millers, Univ. of Latvia (Latvia)
Larisa Grigorjeva, Univ. of Latvia (Latvia)


Published in SPIE Proceedings Vol. 3347:
Optical Information Science and Technology (OIST97): Optical Recording Mechanisms and Media
Andrei L. Mikaelian, Editor(s)

© SPIE. Terms of Use
Back to Top